PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer	PolyOne Corporation
Trade Name	Maxxam™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Melt Flow	7.0 g/10 min @Load 21.6 kg, Temperature 190 °C	7.0 g/10 min @Load 47.6 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	29.6 MPa	4290 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	4.0 %	4.0 %	Type I, 51 mm/min; ASTM D638
Flexural Strength	40.0 MPa	5800 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	102 °C @Thickness 3.18 mm	216 °F @Thickness 0.125 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	61.0 °C @Thickness 3.18 mm	142 °F @Thickness 0.125 in	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Mold Temperature	16.0 - 50.0 °C	60.8 - 122 °F

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	General Purpose
Filler / Reinforcement	Glass Fiber Reinforcement
	Unspecified FillerReinfor., 15% Filler by Weight
Forms	Pellets
Generic Material	HDPE
Generic Name	Polyethylene, High Density (HDPE)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications