PolyOne LubriOne™ PC-000/05T-2S Polycarbonate (PC)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ PC-000/05T-2S Polycarbonate (PC).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.23 g/cc	1.23 g/cc	ASTM D792
Water Absorption	0.15 % @Thickness 0.508 mm	0.15 % @Thickness 0.0200 in	@ 24 hrs; ASTM D570
Water Absorption at Saturation	0.35 % @Thickness 0.508 mm	0.35 % @Thickness 0.0200 in	ASTM D570
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.7 MPa	8800 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	7.0 %	7.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.41 GPa	350 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Izod Impact, Notched	2.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	68.0 µm/m-°C	37.8 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	127 °C @Thickness 3.18 mm	261 °F @Thickness 0.125 in	Annealed; ASTM D648
Flammability, UL94	HB	HB	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm	1.00e+17 ohm-cm	ASTM D257

Processing Properties	Metric	English
Melt Temperature	288 - 316 °C	550 - 601 °F
Mold Temperature	54.4 - 121 °C	130 - 250 °F
Drying Temperature	121 °C	250 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Features	Lubricated
Forms	Pellets
Generic Material	PC
Generic Name	Polycarbonate (PC)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Conveyor Parts
	Printer Parts