- PolyOne Geon™ Vinyl Rigid Molding M5705 Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ Vinyl Rigid Molding M5705 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M5705 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 88.9 cm | 35.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 32 % | 32 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 66.9 MPa | 9700 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm @Thickness 3.18 mm, Temperature -18.0 °C |
1.70 ft-lb/in @Thickness 0.125 in, Temperature -0.400 °F |
Injection Molded; ASTM D256A |
| 1.60 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
3.00 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A | |
| 6.90 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
12.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 66.1 °C @Thickness 3.18 mm |
151 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 70.6 °C @Thickness 3.18 mm |
159 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C @Thickness 3.18 mm |
136 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| High Flow | ||
| Medium Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Construction Applications | |
| General Purpose | ||
| Outdoor Applications |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 86110 white 1275 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne Versaflex™ 9555-9 Thermoplastic Elastomer (TPE)
- Gichem GILAC H120X6/VOU ABS Flame Retardant (discontinued **)
- Hexion Bakelite™ PF 6507 Phenolic Formaldehyde Resin, Elasticized, Low Shrinkage, Resistant to High Temperatures, High Mechanical Strength
- Johnson Matthey JM4060 Soft Solder/Flux
- Multibase C6-530 Dow-Corning Class VI Elastomer
- Techmer ES HiFill® PP GF/M30 CC BK 30% Glass/Mineral Filled
- Polyram PlusTek RA601 Nylon 6.6, Heat Resistant
- 3M XG5110 General Purpose Double Coated Tape
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Annealed
Copyright © lookpolymers.com All Rights Reserved