PolyOne Geon™ Vinyl Rigid Molding M4300 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M4300 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 58.4 cm | 23.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | ASTM D2240 |
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 30 % | 30 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.83 GPa | 410 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A |
| 8.50 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
15.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C @Thickness 6.35 mm |
158 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C @Thickness 6.35 mm |
154 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 72.8 °C @Thickness 6.35 mm |
163 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
ALL; UL 94 |
| 5VA @Thickness 1.91 mm |
5VA @Thickness 0.0752 in |
ALL; UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % @Thickness 3.81 mm |
4.0 % @Thickness 0.150 in |
ASTM D1003 |
| Transmission, Visible | 78 % @Thickness 3.81 mm |
78 % @Thickness 0.150 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 204 °C | 390 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 61 | |
| NSF Unspecified Rating | ||
| Appearance | Clear/Transparent | |
| Features | General Purpose | |
| High Impact Resistance | ||
| Medium Flow | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Fluid Handling | |
| General Purpose |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP HBK15030 Polypropylene, Multifiller High Gloss
- Polykemi AB POLYshine PBT D211 PBT, Modified
- PolyOne Nymax™ GF 1204 33 HS Natural Polyamide 66 (Nylon 66)
- Polymer Resources PC/ABS-GP1-[color]-EP General Purpose PC/ABS Alloy, Electroplating Grade
- Mitsubishi Xantar® C CM 206 U Polycarbonate/ABS Blend
- Sharadaa Ceramics ZAP 007 Smart Cast Application
- Hexcel® HexForce™ GA090 Carbon Fabric
- Polyram PlusTek PB500 Nylon 6, Flame Retardant
- Denka VINYKON M1610 PVC, M grade for hard injection molding
Copyright © lookpolymers.com All Rights Reserved