PolyOne Geon™ Vinyl Rigid Molding 6957 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding 6957 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 55.9 cm | 22.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | ASTM D2240 |
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.45 GPa | 355 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 2.52 GPa | 365 ksi | ASTM D790 |
| Izod Impact, Notched | 2.70 J/cm @Thickness 3.18 mm, Temperature -18.0 °C |
5.06 ft-lb/in @Thickness 0.125 in, Temperature -0.400 °F |
Injection Molded; ASTM D256A |
| 5.30 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
9.93 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A | |
| 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C @Thickness 6.35 mm |
156 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 72.2 °C @Thickness 6.35 mm |
162 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 6.35 mm |
153 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 70.0 °C @Thickness 6.35 mm |
158 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
GY; UL 94 |
| V-0 @Thickness 1.53 mm |
V-0 @Thickness 0.0602 in |
Gray |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- RheTech Products FT4802-692UV Thermoplastic Polyolefin, UV Stabilized, RS8 Grey
- Palm Labs Adhesives Turbo Fuse Series 120SI Surface Insensitive (40 Viscosity) Rapid Bonding Adhesive
- Park Electrochemical Nelco® NH9294 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- Overview of materials for Polypropylene with 30% Talc Filler
- Kolon KOCETAL® LF302 Wear Modified Acetal Resin
- Lubriplate Super GPO L0754 Heavy-Duty Motor Oil Motor Oil & Transmission Fluid
- Dow Latex XZ 92199.00 Experimental Latex
- EMS-Grivory Grivory® GVX-6 H black 9915 PA*-GF60
- Ashley Polymers Ashlene® 525 Nylon 66
- 3M Scotch-Weld™ 3794 Hi Tack PSA Bulk only Adhesive
Copyright © lookpolymers.com All Rights Reserved