PolyOne Geon™ Vinyl Rigid Extrusion L8230 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L8230 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 46.7 MPa | 6770 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 86.7 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 3.24 GPa | 470 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| Dart Drop Total Energy | 23.1 J/cm @Temperature 23.0 °C |
0.0433 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 23.1 J/cm @Temperature 23.0 °C |
0.0433 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 76.0 µm/m-°C | 42.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.1 °C @Thickness 3.18 mm |
106 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 10341 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Handles | |
| Profiles |
Users viewing this material also viewed the following:
- RheTech Products G30P100-01 30% Glass Fiber Reinforced Polypropylene, Black
- LATI LARPEEK 10 G/50 50% Glass Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Gromax CFG33-RN13N1 Nylon 6 33% Glass Filled (Dry)
- Samyang Tripet® 2550GN30 Polyethylene Terephthalate, 30% Glass Fiber Reinforced, Flame Retardant
- CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Dry
- ATI Allvac® Nickelvac® W-722 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age
- Ashley Polymers Ashlene® 195-N2 Acetal
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
- Resinlab® EP1305LV Clear Epoxy Casting Resin
Copyright © lookpolymers.com All Rights Reserved