PolyOne Geon™ Vinyl Rigid Extrusion L7801 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L7801 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 41.3 MPa | 5990 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.90 GPa | 421 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| Izod Impact, Notched | 2.00 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
3.75 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Compression Molded; ASTM D256A |
| 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A | |
| Dart Drop Total Energy | 40.5 J/cm @Temperature 0.000 °C |
0.0759 ft-lb/mil @Temperature 32.0 °F |
Procedure A, C.125; ASTM D4226 |
| 40.5 J/cm @Temperature 0.000 °C |
0.0759 ft-lb/mil @Temperature 32.0 °F |
Procedure B, C.125; ASTM D4226 | |
| 52.0 J/cm @Temperature 23.0 °C |
0.0974 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 | |
| 178 J/cm @Temperature 23.0 °C |
0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.1 °C @Thickness 3.18 mm |
169 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 78.9 °C @Thickness 3.18 mm |
174 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C @Thickness 3.18 mm |
160 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | High Impact Resistance | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 1-41424-33-0000 | ASTM D4216 |
| 16254 | ASTM D1784 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications | |
| Profiles |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® TPE 1502 Conductive Thermoplastic Compound
- SABIC Innovative Plastics Lexan® PC1800R PC (Europe-Africa-Middle East)
- LG Chemical LUCEL N109-AS Antistatic POM, Unreinforced, Standard Viscosity
- Lanxess Durethan® AKV 30 H3.0 000000 Nylon 66, 30% Glass Fibers
- Lehmann & Voss LUVOCOM® 1104-7452 Polyether ketone, with glass fiber, easy flowing
- Eagle Brass 762 Nickel Silver 12%, Spring
- ChevronTexaco Marfak® Heavy Duty 3
- DuPont Performance Polymers Hytrel® 8238 Polyester Elastomer TPC-ET (Unverified Data**)
- American Computer Optics Water White Filter 6 mm
- ATI Allvac® AL 6XN® UNS N08367 Specialty Steel
Copyright © lookpolymers.com All Rights Reserved