PolyOne Geon™ Vinyl Rigid Extrusion L0111 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L0111 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 49.2 MPa | 7140 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.79 GPa | 405 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 85.5 MPa | 12400 psi | ASTM D790 |
| Flexural Modulus | 2.87 GPa | 416 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.599 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 0.430 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.806 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 0.850 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 60.9 J/cm @Temperature 23.0 °C |
0.114 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 192 J/cm @Temperature 23.0 °C |
0.360 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C @Thickness 3.18 mm |
154 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | FDA Food Contact, Unspecified Rating | |
| Appearance | Clear/Transparent | |
| Features | Food Contact Acceptable | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13453 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |
Users viewing this material also viewed the following:
- RheTech Products FT2500-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black
- Precision Polymer Engineering Kemex™ V76W
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N990 Filler
- Spartech Korad® SP-9071 FR/ABS Flame Retardant Sheet
- Lubrizol Estane® MVT 90AF3 Thermoplastic Polyurethane, Moisture Vapor Transmission
- Borealis Daploy™ SF203HMS High Melt Strength Polypropylene for Extrusion Coating
- ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin (Asia Pacific Grade)
- Overview of materials for Polybutylene Terephthalate (PBT), Carbon Black Filled
Copyright © lookpolymers.com All Rights Reserved