PolyOne Geon™ Vinyl Rigid Extrusion 87180 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Vinyl Rigid Extrusion 87180 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc	1.42 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	83	83	15 sec; ASTM D2240
Tensile Strength, Yield	44.7 MPa	6480 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	3.30 GPa	479 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	83.6 MPa	12100 psi	ASTM D790
Flexural Modulus	3.10 GPa	450 ksi	ASTM D790
Izod Impact, Notched	1.90 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.56 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Compression Molded, Across Flow; ASTM D256A
	2.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.75 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Compression Molded, Flow; ASTM D256A
Dart Drop Total Energy	64.9 J/cm @Temperature 23.0 °C	0.122 ft-lb/mil @Temperature 73.4 °F	Procedure A, C.125; ASTM D4226
	159 J/cm @Temperature 23.0 °C	0.298 ft-lb/mil @Temperature 73.4 °F	Procedure B, C.125; ASTM D4226

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	63.0 µm/m-°C	35.0 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C @Thickness 3.18 mm	158 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 0.899 mm	V-0 @Thickness 0.0354 in	ALL; UL 94
	5VA @Thickness 1.50 mm	5VA @Thickness 0.0591 in	ALL; UL 94

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 193 °C	360 - 379 °F

Descriptive Properties	Value	Comments
Agency Ratings	NSF 51
Ease of Sizing	Good
Features	General Purpose
	High Impact Resistance
Forms	Pellets
Generic Material	PVC, Rigid
Generic Name	Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method	Extrusion
PVC Cell Classification	13364	ASTM D1784
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	General Purpose
	Profiles