Seals Eastern 5795 Fluorocarbon-Elastomer

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Seals Eastern, Inc
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Seals Eastern 5795 Fluorocarbon-Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Seals Eastern's formulated VitonÂ® elastomers can be utilized in seals, o-rings, gaskets, packings and other applications where thermal stability and chemical resistance are required.Features:Type 3 (Viton GFLT)Low temperature serviceFuel and chemical resistanceVitonÂ® is a registered trademark of DuPont. Information provided by Seals Eastern.

Physical Properties	Metric	English	Comments
Specific Gravity	1.88 g/cc	1.88 g/cc	ASTM D297, 15

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	>= 87	>= 87	ASTM D2240
	93	93	Average; ASTM D2240
	93	93	Dry Heat Aging 392Â°F; 70 hr; ASTM D865
	94	94	Dry Heat Aging 392Â°F; 168 hr; ASTM D865
	94	94	Dry Heat Aging 392Â°F; 336 hr; ASTM D865
Tensile Strength	>= 12.30 MPa	>= 1784 psi	ASTM D412 Method A
	13.76 MPa	1996 psi	Average; ASTM D412 Method A
	15.28 MPa	2216 psi	Dry Heat Aging 392Â°F; 168 hr; ASTM D865
	15.42 MPa	2236 psi	Dry Heat Aging 392Â°F; 70 hr; ASTM D865
	16.38 MPa	2375 psi	Dry Heat Aging 392Â°F; 336 hr; ASTM D865
Tensile Stress	5.75 MPa @Strain 25.0 %	834 psi @Strain 25.0 %	Average; ASTM D412 Method A
	>= 8.094 MPa @Strain 50.0 %	>= 1174 psi @Strain 50.0 %	ASTM D412 Method A
	8.391 MPa @Strain 50.0 %	1217 psi @Strain 50.0 %	Average; ASTM D412 Method A
Elongation at Break	>= 85 %	>= 85 %	ASTM D412 Method A
	94 %	94 %	Average; ASTM D412 Method A
	103 %	103 %	Dry Heat Aging 392Â°F; 336 hr; ASTM D865
	107 %	107 %	Dry Heat Aging 392Â°F; 70 hr; ASTM D865
	109 %	109 %	Dry Heat Aging 392Â°F; 168 hr; ASTM D865
Modulus of Elasticity	0.0425 GPa	6.16 ksi	Calculated; ASTM D412 Method A
Shear Modulus	0.01415 GPa	2.053 ksi	Calculated; ASTM D412 Method A
Secant Modulus	0.03939 GPa	5.713 ksi	ASTM D412 Method A
Tear Strength Test	201	201	psi; ASTM D624, Die B
Compression Set	20 % @Temperature 200 Â°C, Time 79200 sec	20 % @Temperature 392 Â°F, Time 22.0 hour	ASTM D395, Test B
	24 % @Temperature 200 Â°C, Time 252000 sec	24 % @Temperature 392 Â°F, Time 70.0 hour
	37 % @Temperature 200 Â°C, Time 1.21e+6 sec	37 % @Temperature 392 Â°F, Time 336 hour

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	204 Â°C	400 Â°F
Minimum Service Temperature, Air	-31.1 Â°C	-24.0 Â°F	Retraction Temperature, TR10; ASTM D1329

Processing Properties	Metric	English	Comments
Shelf Life	240 Month	240 Month

Descriptive Properties	Value	Comments
Strain Energy/ Unit Volume at 20% Elongation (psi)	110	ASTM D412 Method A