PolyOne Geon™ Vinyl Flexible A65M0 Polyvinyl Chloride, Flexible (PVC, Flexible)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Flexible A65M0 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recommended for interior applications.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.023 - 0.027 cm/cm | 0.023 - 0.027 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | 15 sec; ASTM D2240 |
| 65 | 65 | ASTM D2240 | |
| Tensile Strength at Break | 12.4 MPa | 1800 psi | 510 mm/min; ASTM D638 |
| Tensile Strength | 6.76 MPa @Strain 100 % |
980 psi @Strain 100 % |
510 mm/min; ASTM D638 |
| Elongation at Break | 340 % | 340 % | 510 mm/min; ASTM D638 |
| Tear Strength | 43.8 kN/m | 250 pli | Die C, 510 mm/min; ASTM D624 |
| Compression Set | 45 % @Temperature 23.0 °C, Time 79200 sec |
45 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -34.4 °C | -29.9 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % @Thickness 1.91 mm |
3.0 % @Thickness 0.0750 in |
ASTM D1003 |
| Transmission, Visible | 85 % @Thickness 1.91 mm |
85 % @Thickness 0.0750 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 174 - 179 °C | 345 - 354 °F | |
| 188 - 199 °C | 370 - 390 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | High Gloss | |
| Low to No Migration | ||
| Forms | Pellets | |
| Generic Material | PVC, Flexible | |
| Generic Name | Polyvinyl Chloride, Flexible (PVC, Flexible) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: 20-30 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Schott SF6HT Glass
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 100 lb
- SABIC Innovative Plastics ULTEM 1000P PEI (Europe-Africa-Middle East)
- Formosa Plastics Formolene® 5143H Homopolymer Polypropylene
- Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Machined Parts
- ExxonMobil 825 Mobil SHC 800 Series
- Arlon 51576S020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Less Common Metals LaNi5 Cast Hydrogen Storage
Copyright © lookpolymers.com All Rights Reserved