Category | Polymer , Thermoplastic , Vinyl (PVC) |
Manufacturer | PolyOne Corporation |
Trade Name | Elastamax™ |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | PolyOne Elastamax™ HTE 3070 Polyvinyl Chloride + NBR (PVC+NBR).pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 68 | 68 | 15 sec; ASTM D2240 |
Tensile Strength at Break | 16.9 MPa | 2450 psi | Type IV, 510 mm/min; ASTM D638 |
Tensile Strength | 5.87 MPa @Strain 100 % |
851 psi @Strain 100 % |
Type IV, 510 mm/min; ASTM D638 |
12.6 MPa @Strain 300 % |
1830 psi @Strain 300 % |
Type IV, 510 mm/min; ASTM D638 | |
Elongation at Break | 400 % | 400 % | Type IV, 510 mm/min; ASTM D638 |
Tear Strength | 41.9 kN/m | 239 pli | Die C, 510 mm/min; ASTM D624 |
Compression Set | 53 % @Temperature 70.0 °C, Time 79200 sec |
53 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395A |
58 % @Temperature 100 °C, Time 79200 sec |
58 % @Temperature 212 °F, Time 22.0 hour |
ASTM D395A |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Brittleness Temperature | -56.0 °C | -68.8 °F | ASTM D746 |
Descriptive Properties | Value | Comments |
---|---|---|
Appearance | Natural Color | |
Features | General Purpose | |
Forms | Pellets | |
Generic Material | PVC+NBR | |
Generic Name | Polyvinyl Chloride + NBR (PVC+NBR) | |
Processing Method | Extrusion | |
Injection Molding | ||
Regional Availability | Africa & Middle East | |
Asia Pacific | ||
Europe | ||
North America | ||
South America | ||
Uses | Automotive Applications | |
Construction Applications | ||
General Purpose | ||
Industrial Applications |