- PolyOne Edgetek® SF-35GF-15MC/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
PolyOne Edgetek® SF-35GF-15MC/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-35GF-15MC/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 g/cc | 1.77 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 114 MPa | 16500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 299 - 332 °C | 570 - 630 °F | Molding |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Zytel® FR70M30V0 BK010 Nylon 66 (Unverified Data**)
- Huntsman Araldite EPN 1139 Epoxy Phenol Novolac
- Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced
- Iran Petrochemical (PCC) BL8 HM 7745 High Density Polyethylene
- Techmer ES Electrablend® PPS 06001
- Dow Corning SYL-OFF® 7012 RELEASE MODIFIER
- Abatron AboCast 8502-7/AboCure 8502-7 Colorless, Low-Exotherm Epoxy Casting Compound
- Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66
- CENTROPLAST CENTROGUARD Polyoxymethylene, Antimicrobial
- Shinkong Synthetic Fibers Shinite® D201 PBT
Copyright © lookpolymers.com All Rights Reserved