PolyOne Edgetek® QT-20MN/000 natural HI Syndiotactic Polystyrene (SPS)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® QT-20MN/000 natural HI Syndiotactic Polystyrene (SPS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc @Temperature 23.0 °C |
0.0434 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage, Flow | <= 0.013 cm/cm @Thickness 4.00 mm, Temperature 23.0 °C |
<= 0.013 in/in @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded, Bergmann Method; No Standard |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
Type I, 5.0 mm/min; ISO 527 |
| Elongation at Break | 1.5 % @Temperature 23.0 °C |
1.5 % @Temperature 73.4 °F |
Type I, 5.0 mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
Type I, 5.0 mm/min; ISO 527 |
| Charpy Impact Unnotched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C @Thickness 3.18 mm |
446 °F @Thickness 0.125 in |
Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB | HB | UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 320 °C | 518 - 608 °F | |
| Mold Temperature | 80.0 - 150 °C | 176 - 302 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Filler / Reinforcement | MineralInorganic | |
| Forms | Pellets | |
| Generic Material | SPS | |
| Generic Name | Syndiotactic Polystyrene (SPS) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- NYCOA 534H PA 6
- NCMT NanoPAC™ S301 High Performance Polypropylene Nanocomposite
- DuPont™ Clysar® ABL Polyolefin Shrink Packaging Film, 100 Gauge (discontinued **)
- MarkeTech Magnesium Oxide (MgO) Single Crystal Substrate
- Mearthane Durethaneâ„¢ M DM-650A Foam Polyurethane
- Dow Corning HS II BASE & 10:1, COLORED CATALYST
- Braskem AC59 HDPE Monofilament Polyethylene Homopolymer
- 3M Scotch-Weld™ DP405 LH Epoxy Adhesive
- Radici Radilon® A RV350 (dry) Nylon 66
- Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved