PolyOne Edgetek® PS-30GF/000 Polybutylene Terephthalate (PBT), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PS-30GF/000 Polybutylene Terephthalate (PBT), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hr. Immersion, -; ASTM D570 |
| 0.45 % | 0.45 % | Long-Term Immersion, -; ASTM D570 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 134 MPa | 19500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 13.1 GPa | 1900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Compressive Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 266 °C | 480 - 510 °F | Molding |
| Mold Temperature | 121 °C | 250 °F | |
| Drying Temperature | 107 °C | 225 °F | 4 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Raschig Group RALUPOL® 2100 UP Polyester
- Huntsman IROGRAN® PS 440-200 TPU-Polyester
- Lanxess Durethan® B 40 FKA 000000 Nylon 6, Film Grade
- SABIC Innovative Plastics Valox® 8032UX PBT+PET (Europe-Africa-Middle East)
- Spartech Polypedic A Low Density Polyethylene
- Zhejiang Juner PA-A6-66H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
- Chosun Refractories APM-1 Special Mortar
- AK Steel ASTM A 607 Class 2 Formable, Grade 45K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- 3M Scotchcal™ 8000-114 Graphic Film
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler
Copyright © lookpolymers.com All Rights Reserved