Karina 809D48/1-C-IS-LMP Black PVC Compound
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded |
| Manufacturer | Karina Indústria e Comércio de Plásticos |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Karina 809D48/1-C-IS-LMP Black PVC Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heavy metal free PVC compound recommended for extrusion of coaxial cables jacket. Also recommended for extrusion of automotive flexible tube. Working temperature range: -40°C to +80°C.Information provided by Karina Indústria e Comércio de Plásticos Ltda.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 - 1.39 g/cc | 1.33 - 1.39 g/cc | NBR NM-IEC 60811-1-3 |
| ASTM Color | -1.04 - 0.56 | -1.04 - 0.56 | Color B, ME 12 |
| -0.770 - 0.83 | -0.770 - 0.83 | Color A, ME 12 | |
| 25.1 - 26.7 | 25.1 - 26.7 | Color L, ME 12 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 - 82 @Time 15.0 sec |
78 - 82 @Time 0.00417 hour |
NBR 7456 |
| Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
| >= 12.6 MPa | >= 1820 psi | After 168H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 | |
| Elongation at Break | >= 125 % | >= 125 % | NBR NM-IEC 60811-1-1 |
| >= 125 % | >= 125 % | After 168H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D 746 |
| Flame Spread | <= 1.00 mm/min | <= 0.0394 in/min | ISO 3795 |
| Oxygen Index | >= 25 % | >= 25 % | NBR 6245 |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Cadmium, Cd | <= 0.0050 % | <= 0.0050 % | IEC 62321 |
| Chromium, Cr | <= 0.010 % | <= 0.010 % | IEC 62321 |
| Lead, Pb | <= 0.010 % | <= 0.010 % | IEC 62321 |
| Mercury, Hg | <= 0.010 % | <= 0.010 % | IEC 62321 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | NBR 5403 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Application | General Purpose Hoses | |
| Bromine, Br (%) | < 0.01 | IEC 62321 |
| Maximum Variation of Elongation (%) | 25 | NBR NM-IEC 60811-1-2 |
| Maximum Variation of Tensile Strength (%) | 25 | NBR NM-IEC 60811-1-2 |
Users viewing this material also viewed the following:
- Spartech PP7140 Talc Filled High Impact Copolymer
- Teknor Apex APEX® 1519-45 Polyvinyl Chloride, Flexible
- Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf)
- A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Dow CYCLOTENE™ 3022-63 Bisbenzocyclobutene (BCB) Electronic Resin
- AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Extra Deep Drawing Steel (EDDS), Standard Grade
- Beijing Chemical Industry KAIFA® GL1100 ABS General Purpose Grade
- Beijing Chemical Industry KAIFA® M109-G20 MPPO Resin
- Bulk Molding Compounds tetra-DUR F 4308 Bulk Molding Compound
- SABIC Innovative Plastics LNP VERTON NV008E PC/ABS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved