EMS-Grivory Grivory® L 20 nat PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® L 20 nat PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium viscosity unmodified Polyamide 12Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 % | 1.5 % | ISO 62 |
| Moisture Absorption | 0.700 % | 0.700 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | conditioned, 15s; ISO 868 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
| 55.0 MPa | 7980 psi | dry; ISO 527-1/-2 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
| 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 |
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| 12 % | 12 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.10 GPa | 160 ksi | conditioned; ISO 527-1/-2 |
| 1.40 GPa | 203 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | dry; ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS |
| 150 °C | 302 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Food contact | EU Requirements | |
| FDA | ||
| Form | Granules | |
| Industry & Consumer goods | Medical devices | |
| Medical | USP VI | |
| Packaging | Non oriented film | |
| Processing | Film Extrusion | |
| Injection Molding | ||
| Other Extrusion |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512S (842S) (UF) Synthetic Oil
- Plastcom SLOVASTER® B1 HML GF 20 PBT, 20% glass fibre
- Eastman 5223 LDPE 6% VA Copolymer, High Clarity, Ultra-High Impact Film Resin (discontinued **)
- Karina E 10/31-RG-GE White Color Concentrate for PVC
- SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific)
- Teknor Apex APEX® 90-P513A-65-NT Polyvinyl Chloride+PUR
- Wellman Wellamid® FRGF1827-BK1 10% Glass Fiber Reinforced Flame Retardant Nylon 66
- Buckeye Polymers BP RPP 3009 GK3 BLK Polypropylene, Glass Filled
Copyright © lookpolymers.com All Rights Reserved