PolyOne Edgetek® PK-1000 Polyetheretherketone (PEEK)  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® PK-1000 Polyetheretherketone (PEEK)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Description/Features:PEEK (Polyetheretherketone)UnfilledHi-TempApplications: Multi-purposeProcessing Method: Injection MoldingInformation provided by PolyOne Corporation
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Water Absorption 0.50 %

@Thickness 3.17 mm
0.50 %

@Thickness 0.125 in
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0070 - 0.0080 cm/cm
0.0070 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 100 MPa
14500 psi
Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
Elongation at Break 50 - 60 %
50 - 60 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 4.48 GPa
650 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 4.48 GPa
650 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
1.20 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 371 - 399 °C
700 - 750 °F
Molding