Schmolz + Bickenbach Formadur® 2312 (Ultra Holder) Plastic Mold Steel

Category Metal , Ferrous Metal , Tool Steel , Mold Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name Formadur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach Formadur® 2312 (Ultra Holder) Plastic Mold Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Formadur® 2312 is a pre-hardened single melt Extra Fine Structure (EFS) plastic mold steel and Re-sulphurized to improve machinabilityCharacteristics: Excellent machinability compared to Formadur® 2311Applications: Injection molds where surface finish is not critical, Mold bases, Die holders, Ejector plates and Rubber moldInformation provided by Schmolz + Bickenbach
Physical Properties Metric English Comments
Density 7.83 g/cc
0.283 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 28

@Treatment Temp. 700.0 °C,
Time 7200 sec
 28

@Treatment Temp. 1292 °F,
Time 2.00 hour
36

@Treatment Temp. 600.0 °C,
Time 7200 sec
 36

@Treatment Temp. 1112 °F,
Time 2.00 hour
42

@Treatment Temp. 500 °C,
Time 7200 sec
 42

@Treatment Temp. 932 °F,
Time 2.00 hour
46

@Treatment Temp. 400 °C,
Time 7200 sec
 46

@Treatment Temp. 752 °F,
Time 2.00 hour
48

@Treatment Temp. 300 °C,
Time 7200 sec
 48

@Treatment Temp. 572 °F,
Time 2.00 hour
50

@Treatment Temp. 200 °C,
Time 7200 sec
 50

@Treatment Temp. 392 °F,
Time 2.00 hour
51

@Treatment Temp. 100 °C,
Time 7200 sec
 51

@Treatment Temp. 212 °F,
Time 2.00 hour
Tensile Strength 924 MPa
134000 psi
32 HRC
848 MPa

@Treatment Temp. 700.0 °C
 123000 psi

@Treatment Temp. 1292 °F
 28 HRC
1140 MPa

@Treatment Temp. 600.0 °C
 165000 psi

@Treatment Temp. 1112 °F
 36 HRC
1330 MPa

@Treatment Temp. 500 °C
 193000 psi

@Treatment Temp. 932 °F
 42 HRC
1480 MPa

@Treatment Temp. 400 °C
 215000 psi

@Treatment Temp. 752 °F
 46 HRC
1570 MPa

@Treatment Temp. 300 °C
 228000 psi

@Treatment Temp. 572 °F
 48 HRC
1670 MPa

@Treatment Temp. 200 °C
 242000 psi

@Treatment Temp. 392 °F
 50 HRC
1730 MPa

@Treatment Temp. 100 °C
 251000 psi

@Treatment Temp. 212 °F
 51 HRC
Thermal Properties Metric English Comments
CTE, linear 12.2 µm/m-°C

@Temperature 21.1 - 93.3 °C
 6.80 µin/in-°F

@Temperature 70.0 - 200 °F
13.0 µm/m-°C

@Temperature 21.1 - 204 °C
 7.20 µin/in-°F

@Temperature 70.0 - 400 °F
13.7 µm/m-°C

@Temperature 21.1 - 302 °C
 7.60 µin/in-°F

@Temperature 70.0 - 575 °F
Thermal Conductivity 38.9 W/m-K

@Temperature 302 °C
 270 BTU-in/hr-ft²-°F

@Temperature 575 °F
39.8 W/m-K

@Temperature 100 °C
 276 BTU-in/hr-ft²-°F

@Temperature 212 °F
40.3 W/m-K

@Temperature 204 °C
 280 BTU-in/hr-ft²-°F

@Temperature 400 °F
Component Elements Properties Metric English Comments
Carbon, C 0.40 %
0.40 %
Chromium, Cr 1.9 %
1.9 %
Iron, Fe 95.95 %
95.95 %
Manganese, Mn 1.5 %
1.5 %
Molybdenum, Mo 0.20 %
0.20 %
Sulfur, S 0.050 %
0.050 %
Processing Properties Metric English Comments
Annealing Temperature 710 - 740.6 °C
1310 - 1365 °F
Cooling: Furnace; < 235 HB