PolyOne Edgetek® ES-30GF/000 Black Polyethersulfone (PESU)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-30GF/000 Black Polyethersulfone (PESU).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Edgetek™ ES-30GF/000 Black XP120031Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | 5.1 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 197 MPa | 28600 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 3.18 mm |
419 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 3.18 mm |
401 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 340 - 380 °C | 644 - 716 °F | |
| Mold Temperature | 140 - 160 °C | 284 - 320 °F | |
| Drying Temperature | 150 - 160 °C | 302 - 320 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| Good Strength | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PESU | |
| Generic Name | Polyethersulfone (PESU) | |
| Processing Method | Injection Molding | |
| Regional Availability | Asia Pacific | |
| Uses | Automotive Applications | |
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N330 Filler
- Indium Corp. Indalloy 13 Indium Solder Alloy
- Karina 806-10/236-H-ISE White PVC Compound
- Lehmann & Voss LUVOCOM® 1105-0918/BL PEEK, with glass fiber
- Hexcel® HexWeb® HRH-10/F35 - 2.5 Nonmetallic Flex-Core Honeycomb
- Asahi Glass Fluon® P-66P PFA Perfluoropolymer
- Atom Adhesives AA-BOND F123 Epoxy Adhesive
- Arlon T2040-B004 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
- Asahi Kasei Xyron® G702V Modified Polyphenylene Ether
- Ashley Polymers Ashlene® D925 Nylon 12
Copyright © lookpolymers.com All Rights Reserved