- PolyOne Edgetek® ES-20GF-15GM/000 Polyethersulfone - 20% Glass Fiber - 15% Milled Glass (discontinued **)
PolyOne Edgetek® ES-20GF-15GM/000 Polyethersulfone - 20% Glass Fiber - 15% Milled Glass (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-20GF-15GM/000 Polyethersulfone - 20% Glass Fiber - 15% Milled Glass
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0035 cm/cm @Thickness 3.17 mm |
0.0030 - 0.0035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | ASTM D638 |
| Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 - 0.960 J/cm @Thickness 6.35 mm |
1.20 - 1.80 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.92 µm/m-°C @Temperature 20.0 °C |
14.40 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 669 - 720 °F | Stock |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F |
Users viewing this material also viewed the following:
- 3M Dyneon™ TFM™ 4212 Modified PTFE, 10% Electrocarbon Filled (discontinued **)
- Intercontinental Polymers HoPBT 303 HoPBT Polymer Type - Clear, Polyester Pellets
- Momentive Performance Materials RTV6186 Clear Potting/Encapsulating Gel
- Lavergne VYPET VNT 615 PET 15% Glass Reinforced
- Hexcel® HexForce™ 6781HT Fiber Glass Fabric
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
- BCC Products DP-11-90 Urethane Casting
- ATI Wah Chang Hafnium Oxide, HfO2
- 3M FM04E Clear Polyester Label Product
- Ashley Polymers Ashlene® R190H2 Acetal
Copyright © lookpolymers.com All Rights Reserved