PolyOne Edgetek® AM-20CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-20CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Thickness 3.17 mm |
0.40 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 179 MPa | 26000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 19.0 GPa | 2750 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 269 MPa | 39000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.40 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 293 °C | 560 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
Users viewing this material also viewed the following:
- Niche Polymer PA6GF13BK Nylon 6, 13% Glass Fiber Filled
- Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film
- Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon
- Borealis BS2581 High Density Polyethylene for Blow Molding
- Polyram PlusTek PB330I6 Nylon 6 for Injection Molding, 30% Mineral and Glass-fiber Filled
- E-Polymers TEKASTER® F100 low-mid viscosity PBT
- 3M 2A804 High Performance Temporary Surface Protection Tape
- ArcelorMittal HSLA 320 High strength low alloy steel for cold forming, Hot Rolled
- Total Lacqtene® 1025 FH 24 LDPE blown film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved