Polimeri Europa SINKRAL F233 ABS, Heat Stabilized  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL F233 ABS, Heat Stabilized  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,105-15-16-25 Medium heat injection moulding grade having high flow and good thermal stability during processing. Widely used in the domestic appliance sector especially for intricate parts in close proximity to heat sources (front panels, frames of washing machines and dishwashers).Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 12 g/10 min

@Load 10.0 kg,
Temperature 220 °C
12 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min
Elongation at Break 25 %
25 %
Nominal
Elongation at Yield 3.0 %
3.0 %
50 mm/min
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min
Charpy Impact Unnotched 14.0 J/cm²
66.6 ft-lb/in²
11.0 J/cm²

@Temperature -30.0 °C
52.4 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C
207 °F
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Vicat Softening Point 101 °C
214 °F
50°C/hr; 50N
Glass Transition Temp, Tg 108 °C
226 °F
10°C/min test
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.7

@Frequency 100 Hz
2.7

@Frequency 100 Hz
3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0070

@Frequency 1e+6 Hz
0.0070

@Frequency 1e+6 Hz
0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V