Polimeri Europa EDISTIR N1670 Polystyrene (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR N1670 Polystyrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,E,095-06 General purpose polystyrene with good flow and good heat resistance. Recommended for extrusion in blend with HIPS or clear SBS for thermoformed packaging. Applications: Food packaging articles as drink and dairy cups, plates, trays.Unfilled. Suitable for Sheet Extrusion, Thermoforming. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | 5 mm/min |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min |
| Tensile Modulus | 3.28 GPa | 476 ksi | 1 mm/min |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | 95.0 °C | 203 °F | 10°C/min test |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Manufacturer specifies 'transparent' but doesn't quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| Comparative Tracking Index | 400 V | 400 V |
Users viewing this material also viewed the following:
- Polimeri Europa Intene® 40 AF Butadiene Rubber
- SABIC Innovative Plastics Lexan® SLX1482T PC Copolymer (Asia Pacific)
- Industeel SOLEIL C5 13% Cr 4 Ni Martensitic Stainless Steel with Improved Toughness
- Kraton® FG1901 + PA-6 blend (20/80)
- Master Bond Mastersil 801 One Component, Room Temperature Curing, Silicone System
- TIMCAL TIMREX® LSG6 Natural Graphite
- DuPont Teijin Films Mylar® RB43 Polyester Film, 100 Gauge
- Advanced Ceramics ALC 1081 (C-786) Alumina
- BASF Ultramid® B36 LN 0.04 mm Cast Film Cold Chillroll
- Breplast Bretene SP Polypropylene / Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved