Plenco 6990 Phenolic, Briquette, Injection Molded
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Glass Filled |
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 6990 Phenolic, Briquette, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.790 g/cc | 0.0285 lb/in³ | ASTM D1895 |
| Density | 1.77 g/cc | 0.0639 lb/in³ | ASTM D792 |
| Water Absorption | 0.071 % | 0.071 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00275 cm/cm | 0.00275 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.38 % | 0.38 % | ASTM D638 |
| Tensile Modulus | 16.2 GPa | 2350 ksi | ASTM D638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 14.6 GPa | 2120 ksi | ASTM D790 |
| Compressive Strength | 156 MPa | 22600 psi | ASTM D695 |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.296 J/cm² | 1.41 ft-lb/in² | ASTM D256 |
| Impact | 172 | 172 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 236 °C | 457 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.500 mm |
V-0 @Thickness 0.0197 in |
|
| Shrinkage | 0.068 % | 0.068 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.20e+11 ohm-cm | 8.20e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.5 | 5.5 | ASTM D150 |
| Dielectric Strength | 14.1 kV/mm | 358 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.062 | 0.062 | ASTM D150 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
Users viewing this material also viewed the following:
- Nyco NYAD® M400 Wollastonite
- Quadrant EPP Ertacetal® C POM-C, extruded (ISO Data)
- PolyOne Geon™ Vinyl Flexible B8000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kingfa LONOY 2100 LT PC/PET Alloy
- Covestro Apec® 1703 Polycarbonate
- Dow Tyrin® CM0836 Formulation
- 3M 7000 Series Copper Roofing Granule (Little Rock)
- Axiall 22851 Coax & Telecom Flexible PVC
- Asahi Kasei Thermylon® NSG-440A 60% Ceramic and Glass Fiber Reinforced
- Mitsui Fybrel® UL 410 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
Copyright © lookpolymers.com All Rights Reserved