PlastxWorld CEVIAN®-V 320 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | PlastxWorld, Inc. |
| Trade Name | CEVIAN®-V |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastxWorld CEVIAN®-V 320 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Impact ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 39.3 MPa | 5700 psi | ASTM 638 |
| Flexural Yield Strength | 63.4 MPa | 9200 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 3.52 J/cm @Thickness 3.17 mm |
6.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 1.76 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
3.30 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.2 µm/m-°C @Temperature 20.0 °C |
49.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | 0.5 inch; ASTM D648 |
| Vicat Softening Point | 93.0 °C | 199 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- 3M Dyneon™ TF 5039 PTFE Dispersion (discontinued **)
- Microcell Composite Company CELLOMER® S-2110D SBS Rubber Foam
- Lucent Polymers TPP-310 Polypropylene, 10% Talc Filled, Impact Modified
- Spartech 3030-10004 PVC and Alloy Products for Wire and Cable
- Styrolution Luran® S 776 SE ASA
- SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK (Asia Pacific)
- ExxonMobil Diol 13 RD 40
- EMS-Griltech Griltex® D 1357E Copolyester Hotmelt Adhesive (Apparel Interlinings)
- A. Schulman POLYBLAK™ 4651SF Universal Black Color Concentrate, 50% Carbon Black in EVA
- HP Alloys Alloy 718, 30% Cold Worked
Copyright © lookpolymers.com All Rights Reserved