E-Polymers SEPAZ® C230GI 30% Glass Fiber Reinforced Good Impact LCP Resin

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® C230GI 30% Glass Fiber Reinforced Good Impact LCP Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding productivity. SEPAZ LCP has a unique attribute in that the thinner the product becomes, the greater the mechanical strength. SEPAZ LCP finds uses in connectors, sensors and other electronic components and CD pick-up parts, and in copying machine and fax components in office and audio-visual equipment.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.62 g/cc
1.62 g/cc
ASTM D792
Linear Mold Shrinkage 0.00 cm/cm
0.00 in/in
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength 150.1 MPa
21770 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Flexural Strength 183.45 MPa
26607 psi
ASTM D790
Flexural Modulus 13.1 GPa
1900 ksi
ASTM D790
Izod Impact, Notched 2.16 J/cm
4.04 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Thickness 1.60 mm
7.78 µin/in-°F

@Thickness 0.0630 in
ASTM D696
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Thickness 1.60 mm
20.0 µin/in-°F

@Thickness 0.0630 in
ASTM D696
Melting Point 352 °C
666 °F
ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 289 °C
552 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm

@Thickness 1.60 mm
610 kV/in

@Thickness 0.0630 in
ASTM D149
Dissipation Factor 0.029

@Frequency 1.00e+6 Hz
0.029

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 365 - 375 °C
689 - 707 °F
Mold Temperature 30.0 - 150 °C
86.0 - 302 °F