Piezo Kinetics 406 Lead Zirconate Titanate Piezoelectric

Category	Ceramic , Oxide , Titanium Oxide , Zirconium Oxide , Piezoelectric
Manufacturer	Piezo Kinetics, Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Piezo Kinetics 406 Lead Zirconate Titanate Piezoelectric.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Denoted as Navy Type I, it is designed to serve as a driver where high power and low losses are dictated by design. It is primarily well suited for ultrasonic cleaners and sonars. PKI 406 is suitable for medical applications.Elastic Compliance s11E (x 10-12 m²/n): 14.1.Elastic Compliance s33E (x 10-12 m²/n): 16.1.Property data at 25°C. Information supplied by Piezo Kinetics, Inc.

Physical Properties	Metric	English	Comments
Density	7.70 g/cc	0.278 lb/in³

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	72.0 GPa	10400 ksi
Poissons Ratio	0.22	0.22
Shear Modulus	30.0 GPa	4350 ksi	calculated

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	150 °C	302 °F	Maximum Operating Temperature

Electrical Properties	Metric	English
Curie Temperature	300 °C	572 °F
Dielectric Constant	1500 @Frequency 1000 Hz	1500 @Frequency 1000 Hz
Dissipation Factor	0.0050 @Frequency 1000 Hz	0.0050 @Frequency 1000 Hz
Piezoelectric Longitudinal Coupling Factor, k33	0.70	0.70
Piezoelectric Transverse Voltage Coefficient, d31, 10^-12 m/V	-150	-150
Piezoelectric Shear Charge Coefficient, d15, 10^-12 m/V	500	500
Piezoelectric Longitudinal Voltage Coefficient, g33, 10^-3 V-m/N	24.1	24.1
Piezoelectric Planar Coupling Factor, kp	0.55	0.55
Piezoelectric Mechanical Q	600	600
Piezoelectric Shear Coupling Factor, k15	0.67	0.67
Piezoelectric Longitudinal Charge Coefficient, d33, 10^-12 m/V	320	320
Piezoelectric Transverse Voltage Coefficient, g31, 10^-3 V-m/N	-11.3	-11.3
Piezoelectric Shear Voltage Coefficient, g15, 10^-3 V-m/N	37.7	37.7
Piezoelectric Transverse Coupling Factor, k31	0.35	0.35