UBE UBEPOL BR340L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR340L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | ASTM D412 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D412 |
| Elongation at Break | 510 % | 510 % | ASTM D412 |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | ASTM D412 |
| 200% Modulus | 0.00530 GPa | 0.769 ksi | ASTM D412 |
| 300% Modulus | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| Rebound | 56 % | 56 % | BS.903,PART22 |
| Tear Strength | 45.0 kN/m | 257 pli | ASTM D624 |
| Abrasion | 102 | 102 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 191 | 191 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 16 % | 16 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 3000 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 10% | ASTM D623 (34°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 18 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E70D Ethylene Propylene Rubber
- Lehmann & Voss LUVOCOM® 20-8368 Polyphthalamide, with carbon fiber and PTFE
- Lubriplate FMO 150 AW USP Mineral Oil-Based Food Machinery Grade Oil
- Kaiser 7068 T76, T76511 Rod & Bar
- Karina CAK 65-48/1 Black PVC Compound
- Michelman® Michem® Emulsion 72040 Nonionic polyethylene wax emulsion
- Williams Advanced Alloys Wambraze™ WB1005 Solder
- California Fine Wire Nickel 211 (Nickel Manganese Alloy)
- Akzo Nobel Trigonox® EHP-C75 Polymerization Initiator
- BASF Pluracol® P1010 Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved