- Phillips Sumika Marlex® ABF-300 High Flow Thermoplastic Olefin (discontinued **)
Phillips Sumika Marlex® ABF-300 High Flow Thermoplastic Olefin (discontinued **)
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Phillips Sumika Marlex® ABF-300 High Flow Thermoplastic Olefin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive exterior fasciasInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc @Thickness 3.17 mm |
0.0322 lb/in³ @Thickness 0.125 in |
injection molded specimen; ISO 1133 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 | 56 | ISO 868 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min, 1/8" thick injection molded specimen; ISO 1183 |
| Flexural Modulus | 0.965 GPa @Thickness 3.17 mm |
140 ksi @Thickness 0.125 in |
injection molded specimen, 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² @Thickness 3.17 mm, Temperature -40.0 °C |
2.14 ft-lb/in² @Thickness 0.125 in, Temperature -40.0 °F |
ISO 180 |
| 45.0 kJ/m² @Thickness 3.17 mm, Temperature 23.0 °C |
21.4 ft-lb/in² @Thickness 0.125 in, Temperature 73.4 °F |
ISO 180 | |
| Impact Test | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
Instrumented, 2.2 m/s, ductile; ASTM 3763 |
| 29.0 J @Temperature -30.0 °C |
21.4 ft-lb @Temperature -22.0 °F |
Instrumented, 2.2 m/s, ductile; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C @Thickness 3.17 mm |
174 °F @Thickness 0.125 in |
injection molded specimen; ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C @Thickness 3.17 mm |
118 °F @Thickness 0.125 in |
injection molded specimen; ISO 75 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B BT Polyethylene Terephthalate
- Polycasa Acryl® G 55 Acrylic, Injection Molding Grade
- NIZHNEKAMSKNEFTEKHIM PE 4131L (314F4) Linear Low Density Polyethylene
- DuPont Nucrel® 30707HS Ethylene-Acrylic Acid Copolymer Resin for Film and Extrusion Coating (discontinued **)
- Shinil Chemical SHINSTAT PP Electrostatic Control Polymer Sheet Grade
- Plastics Group Polifil® RMC-40V 40% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 6 PHR Varox DBPH-50
- DuPont Performance Polymers Zytel® FR95G25V0NH NC010 Nylon 66 (Unverified Data**)
- 3M Fluorinert™ FC-40 Electronic Liquid
- HP Alloys Nitronic® 60 Austenitic Stainless, Level 5 Cold Worked
Copyright © lookpolymers.com All Rights Reserved