POLYMER SEARCH

Perstorp Compounds Aminel GF Melamine

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Melamine , Melamine Formaldehyde, Molded, Glass Fiber Filler
Manufacturer	Perstorp Compounds
Trade Name	Aminel
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Perstorp Compounds Aminel GF Melamine.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Fiberglass-reinforced melamine material with high dimensional stability, excellent injection properties and high thermal stabilityInformation provided by Perstorp Compounds Inc.

Physical Properties	Metric	English	Comments
Density	1.70 g/cc	0.0614 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0016 cm/cm	0.0016 in/in	DIN 53 464
Linear Mold Shrinkage, Transverse	0.0043 cm/cm	0.0043 in/in

Mechanical Properties	Metric	English	Comments
Flexural Strength	160 - 180 MPa	23200 - 26100 psi	ISO 178
Flexural Modulus	12.0 - 13.0 GPa	1740 - 1890 ksi	ISO 178
Charpy Impact Unnotched	1.50 J/cm²	7.14 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.258 W/m-K	1.79 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi)	>= 270 °C	>= 518 °F	ISO 175
Deflection Temperature at 8.0 MPa	170 °C	338 °F	ISO 175
Flammability, UL94	V-0	V-0
Oxygen Index	>= 30 %	>= 30 %	ASTM D2863
Shrinkage	0.45 %	0.45 %	parallel, Post Shrinkage; DIN 53 464
	0.85 %	0.85 %	transverse, Post Shrinkage

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	DIN 53 483
Surface Resistance	>= 1.00e+11 ohm	>= 1.00e+11 ohm	DIN 53 482
Dielectric Constant	6.0 - 7.0	6.0 - 7.0	DIN 53 483
Dissipation Factor	0.080 @Frequency 1000 Hz	0.080 @Frequency 1000 Hz	tan delta; DIN 53 483
Arc Resistance	>= 130 sec	>= 130 sec	ASTM D495
Comparative Tracking Index	>= 700 V	>= 700 V	IEC 112

Descriptive Properties	Value	Comments
Glow Bar 960°C 180 sec	BH2-5	IEC 707
Water Absorption [mg]	<200	DIN 53 495/23°C 96h

Users viewing this material also viewed the following: