Parker Chomerics CHO-SEAL V6433 Conductive Elastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Parker Chomerics |
| Trade Name | CHO-SEAL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Parker Chomerics CHO-SEAL V6433 Conductive Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Material of choice for extensive fluid resistance; no corrosion resistance.Molded onlyRoHS CompliantInformation provided by Chomerics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 4.55 - 5.05 g/cc | 4.55 - 5.05 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 - 92 | 78 - 92 | ASTM D2240 |
| Tensile Strength at Break | >= 2.76 MPa | >= 400 psi | ASTM D412 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D412 |
| Tear Strength | 12.25 kN/m | 69.90 pli | ASTM D624 |
| Compression Set | <= 45 % @Temperature 100 °C, Time 252000 sec |
<= 45 % @Temperature 212 °F, Time 70.0 hour |
ASTM D395 Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 2.10 W/m-K @Pressure 2.07 MPa |
14.6 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| Minimum Service Temperature, Air | -25.0 °C | -13.0 °F | Flex TR10; ASTM D1329 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 0.0060 ohm-cm | 0.0060 ohm-cm | as supplied without pressure sensitive adhesive; MIL-DTL-83528 |
| Shielding Effectiveness | >= 90 dB @Frequency 2.00e+9 Hz |
>= 90 dB @Frequency 2.00e+9 Hz |
Plane Wave; MIL-DTL-83528 Para.4.6.12 |
| >= 90 dB @Frequency 1.00e+10 Hz |
>= 90 dB @Frequency 1.00e+10 Hz |
Plane Wave; MIL-DTL-83528 Para.4.6.12 | |
| >= 100 dB @Frequency 5.00e+8 Hz |
>= 100 dB @Frequency 5.00e+8 Hz |
E Field; MIL-DTL-83528 Para.4.6.12 | |
| >= 105 dB @Frequency 1.00e+8 Hz |
>= 105 dB @Frequency 1.00e+8 Hz |
E Field; MIL-DTL-83528 Para.4.6.12 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Binder | Fluorocarbon/Fluorosilicone | |
| Filler | Ag/Ni | |
| Heat Aging | <0.008 ohm-cm | 200°C fir 48 hrs; CEPS-0002 |
Users viewing this material also viewed the following:
- Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F)
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1010 PC (Asia Pacific)
- SABIC Innovative Plastics ULTEM 1285 PEI (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East)
- SIDPEC EGYPTENE® HD 5502 GA HDPE Blow Molding
- BASF Lupranate® 253 Isocyanate
- Radici Radilon® A 42 (dry) Nylon 66
- Aremco Ceramacast™ 905 Silicon-Ceramic Potting Compound
Copyright © lookpolymers.com All Rights Reserved