Palm Labs Adhesives TURBO-LOCK SERIES 16 Anaerobic Thread Locking Compound

Category Polymer , Adhesive , Thermoset , Methacrylate , Methacrylate Adhesive
Manufacturer Palm Labs Adhesives
Trade Name TURBO-LOCK SERIES
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Palm Labs Adhesives TURBO-LOCK SERIES 16 Anaerobic Thread Locking Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TURBO-LOCK SERIES 16 is a fast curing, GREEN, medium strength, wicking grade, anaerobic thread-locking compound for bonding and sealing threads, and pre-assembled parts. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbons and many chemicals. Disassembles with heat and hand tools.Applications:IPenetrates threads by capillary action. Medium strength thread-locker.Ideal for sealing hairline cracks, small nuts and bolts.Seals and welds porous metal parts. Localize heating and hand tools are needed for disassembly. Prevents corrosion and leakage.Secure setscrews and other assemblies after settings are completed.Fasteners on vibrating machines or moving components.Meets Military specifications:MIL-S-46163 and MIL-S-22473Part Numbers for this data: 16-001, 16-010, 16-050, 16-250, 16-1000Information provided by Palm Laboratories Adhesives
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
Brookfield Viscosity 12 cP
12 cP
RVT Spindle 3 @ 20 rpm
Mechanical Properties Metric English Comments
Shear Strength >= 5.40 MPa
>= 783 psi
ISO 10123; Compressive, Steel pins and collars
Thermal Properties Metric English Comments
CTE, linear 0.800 µm/m-°C
0.444 µin/in-°F
ASTM D696
Specific Heat Capacity 0.300 J/g-°C
0.0717 BTU/lb-°F
Thermal Conductivity 0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
ASTM C177
Processing Properties Metric English Comments
Cure Time 60.0 - 180 min
1.00 - 3.00 hour
Functional
1440 min
24.0 hour
Full
19.8 min

@Temperature -55.0 - 150 °C
0.330 hour

@Temperature -67.0 - 302 °F
Handling
Shelf Life 24.0 Month
24.0 Month
Descriptive Properties Value Comments
Appearance Green
Chemical Resistance 50% Initial Strength Retained
Motor Oil at 125°C, at 1000hrs
85% Initial Strength Retained
Brake Fluid at 22°C, at 1000hrs
85% Initial Strength Retained
Motor Oil at 125°C, at 500hrs
90% Initial Strength Retained
Gasoline at 22°C, at 500hrs
90% Initial Strength Retained
Brake Fluid at 22°C, at 500hrs
90% Initial Strength Retained
Water/Glycol at 87°C, at 500hrs
90% Initial Strength Retained
Water/Glycol at 87°C, at 1000hrs
90% Initial Strength Retained
Gasoline at 22°C, at 1000hrs
95% Initial Strength Retained
Acetone at 22°C, at 500hrs
95% Initial Strength Retained
Ethanol at 22°C, at 500hrs
95% Initial Strength Retained
Acetone at 22°C, at 1000hrs
95% Initial Strength Retained
Ethanol at 22°C, at 1000hrs
Composition Methacrylate Ester
Torque 10 N.m
Breakaway, M10 steel nuts and bolts N.m, ISO 10964
29 N.m
Prevail, M10 steel nuts and bolts N.m, ISO 10964
30 N.m
Breakloose, pre-torqued to 5 N.m, M10 steel nuts and bolts, ISO 10964
40 N.m
Max Prevail, pre-torqued to 5 N.m, M10 steel nuts and bolts N.m, ISO 10964