Palm Labs Adhesives TURBO-LOCK SERIES 11 Anaerobic Thread Locking Compound

Category	Polymer , Adhesive , Thermoset , Methacrylate , Methacrylate Adhesive
Manufacturer	Palm Labs Adhesives
Trade Name	TURBO-LOCK SERIES
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Palm Labs Adhesives TURBO-LOCK SERIES 11 Anaerobic Thread Locking Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TURBO-LOCK 11 SERIES is a fast curing, BLUE, removable, medium strength, general purpose anaerobic thread-locking compound for bonding and sealing threads. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbons and many chemicals. Disassembles with hand tools.Applications:Ideal for thread locking plated parts, vibration or moving components.Ideal for fasteners between up to ¾” (up to 20 mm) diameters.Locks and seals threaded joints-nuts, screws, and studs.Meets 90% of all nut and bolt thread locking applications.Meets Military specifications: MIL-S-46163Part Numbers for this data: 11-000, 11-001, 11-010, 11-050, 11-250, 11-1000Information provided by Palm Laboratories Adhesives

Physical Properties	Metric	English	Comments
Specific Gravity	1.07 g/cc	1.07 g/cc
Brookfield Viscosity	1200 cP	1200 cP	RVT Spindle 3 @ 20 rpm

Thermal Properties	Metric	English	Comments
CTE, linear	0.800 µm/m-°C	0.444 µin/in-°F	ASTM D696
Specific Heat Capacity	0.300 J/g-°C	0.0717 BTU/lb-°F
Thermal Conductivity	0.100 W/m-K	0.694 BTU-in/hr-ft²-°F	ASTM C177
Flash Point	>= 37.8 °C	>= 100 °F

Processing Properties	Metric	English	Comments
Cure Time	60.0 - 180 min	1.00 - 3.00 hour	Functional
	1440 min	24.0 hour	Full
	10.0 min @Temperature -55.0 - 150 °C	0.167 hour @Temperature -67.0 - 302 °F	Handling
Shelf Life	24.0 Month	24.0 Month

Descriptive Properties	Value	Comments
Appearance	Blue
Chemical Resistance	100% Initial Strength Retained	Acetone at 22°C, at 500hrs
	100% Initial Strength Retained	Ethanol at 22°C, at 500hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 500hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 500hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 500hrs
	100% Initial Strength Retained	Ethanol at 22°C, at 1000hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 1000hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 1000hrs
	80% Initial Strength Retained	Water/Glycol at 87°C, at 1000hrs
	85% Initial Strength Retained	Acetone at 22°C, at 1000hrs
	90% Initial Strength Retained	Water/Glycol at 87°C, at 500hrs
	95% Initial Strength Retained	Gasoline at 22°C, at 1000hrs
Composition	Methacrylate Ester
Max Screw Size	3/4" / 20mm
Torque	1-4 N.m	Prevail, 3/8 x 16 zinc nuts and bolts N.m, ISO 10964
	1-5 N.m	Prevail, 3/8 x 16 cadmium nuts and bolts N.m, ISO 10964
	1-7 N.m	Breakaway, 3/8 x 16 cadmium nuts and bolts N.m, ISO 10964
	2-7 N.m	Breakaway, 3/8 x 16 zinc nuts and bolts N.m, ISO 10964
	3-7 N.m	Prevail, 3/8 x 16 steel nuts and bolts N.m, ISO 10964
	8-17 N.m	Breakaway, 3/8 x 16 steel nuts and bolts N.m, ISO 10964
	8-19 N.m	Breakaway, M10 black oxide steel nuts and bolts N.m, ISO 10964