PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6x

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6x.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Heat Treatment Condition T6x (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.651 - 2.930 g/cc
0.09576 - 0.1058 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 170
>= 170
HV30
Tensile Strength at Break >= 314 MPa

@Temperature 200 °C
 >= 45500 psi

@Temperature 392 °F
>= 411 MPa

@Temperature 150 °C
 >= 59600 psi

@Temperature 302 °F
>= 470 MPa

@Temperature 20.0 °C
 >= 68200 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 260 MPa

@Temperature 260 °C
 >= 37700 psi

@Temperature 500 °F
>= 362 MPa

@Temperature 150 °C
 >= 52500 psi

@Temperature 302 °F
>= 405 MPa

@Temperature 20.0 °C
 >= 58700 psi

@Temperature 68.0 °F
Elongation at Break >= 1.0 %

@Temperature 20.0 °C
 >= 1.0 %

@Temperature 68.0 °F
>= 1.6 %

@Temperature 150 °C
 >= 1.6 %

@Temperature 302 °F
>= 4.1 %

@Temperature 200 °C
 >= 4.1 %

@Temperature 392 °F
Modulus of Elasticity >= 88.0 GPa
>= 12800 ksi
>= 76.0 GPa

@Temperature 200 °C
 >= 11000 ksi

@Temperature 392 °F
>= 80.0 GPa

@Temperature 150 °C
 >= 11600 ksi

@Temperature 302 °F
>= 88.0 GPa

@Temperature 20.0 °C
 >= 12800 ksi

@Temperature 68.0 °F
Poissons Ratio 0.332

@Temperature 20.0 °C
 0.332

@Temperature 68.0 °F
0.334

@Temperature 100 °C
 0.334

@Temperature 212 °F
0.337

@Temperature 150 °C
 0.337

@Temperature 302 °F
0.339

@Temperature 200 °C
 0.339

@Temperature 392 °F
0.342

@Temperature 250 °C
 0.342

@Temperature 482 °F
0.343

@Temperature 300 °C
 0.343

@Temperature 572 °F
Fatigue Strength 225.4 MPa
32690 psi
P50% rotary bending values for 5X10<sup>7</sup> cycles
Shear Modulus 31.0 GPa

@Temperature 250 °C
 4500 ksi

@Temperature 482 °F
31.0 GPa

@Temperature 300 °C
 4500 ksi

@Temperature 572 °F
32.0 GPa

@Temperature 200 °C
 4640 ksi

@Temperature 392 °F
33.0 GPa

@Temperature 150 °C
 4790 ksi

@Temperature 302 °F
34.0 GPa

@Temperature 100 °C
 4930 ksi

@Temperature 212 °F
35.0 GPa

@Temperature 20.0 °C
 5080 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 17.9 - 18.9 µm/m-°C

@Temperature 20.0 - 100 °C
 9.94 - 10.5 µin/in-°F

@Temperature 68.0 - 212 °F
18.5 - 19.5 µm/m-°C

@Temperature 20.0 - 200 °C
 10.3 - 10.8 µin/in-°F

@Temperature 68.0 - 392 °F
19.3 - 20.3 µm/m-°C

@Temperature 20.0 - 300 °C
 10.7 - 11.3 µin/in-°F

@Temperature 68.0 - 572 °F
Specific Heat Capacity 0.860 - 0.900 J/g-°C
0.206 - 0.215 BTU/lb-°F
Thermal Conductivity 116.8 W/m-K

@Temperature 30.0 °C
 810.6 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
117.9 W/m-K

@Temperature 100 °C
 818.2 BTU-in/hr-ft²-°F

@Temperature 212 °F
122.1 W/m-K

@Temperature 200 °C
 847.4 BTU-in/hr-ft²-°F

@Temperature 392 °F
125.7 W/m-K

@Temperature 400 °C
 872.4 BTU-in/hr-ft²-°F

@Temperature 752 °F
131.7 W/m-K

@Temperature 300 °C
 914.0 BTU-in/hr-ft²-°F

@Temperature 572 °F
Melting Point 516 - 738 °C
961 - 1360 °F
Solidus 515.9 - 521.9 °C
960.6 - 971.4 °F
Liquidus 731.5 - 737.5 °C
1349 - 1360 °F
Component Elements Properties Metric English Comments
Aluminum, Al 75 %
75 %
As Balance
Copper, Cu 3.0 %
3.0 %
Iron, Fe 4.0 %
4.0 %
Magnesium, Mg 1.0 %
1.0 %
Silicon, Si 17 %
17 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000750 - 0.00000810 ohm-cm
0.00000750 - 0.00000810 ohm-cm