Oxford Polymers PEI 1000 PEI

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	Oxford Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Oxford Polymers PEI 1000 PEI.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: (Unreinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection Molding Special Characteristics: Colors AvailableInformation provided by Oxford Polymers

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³	ASTM D792
Water Absorption at Saturation	0.250 %	0.250 %	ASTM D570
Linear Mold Shrinkage, Flow	0.00500 - 0.00700 cm/cm @Thickness 3.17 mm	0.00500 - 0.00700 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	103 MPa	15000 psi	ASTM D638
Elongation at Break	3.00 %	3.00 %	ASTM D638
Flexural Strength	152 MPa	22000 psi	ASTM D790
Flexural Modulus	3.45 GPa	500 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Thickness 3.17 mm	1.00 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	206 °C	402 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	349 - 371 °C	660 - 700 °F
Middle Barrel Temperature	354 - 377 °C	670 - 710 °F
Front Barrel Temperature	360 - 382 °C	680 - 720 °F
Nozzle Temperature	360 - 382 °C	680 - 720 °F
Melt Temperature	338 - 427 °C	640 - 800 °F
Mold Temperature	65.6 - 177 °C	150 - 350 °F
Drying Temperature	<= 135 °C	<= 275 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour