Oxford Polymers H-Acetal 20PTFE 20% PTFE Reinforced Homopolymer Acetal (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers H-Acetal 20PTFE 20% PTFE Reinforced Homopolymer Acetal
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% PTFE Reinforced Homopolymer AcetalInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | ASTM D638 |
| Elongation at Break | 13 % | 13 % | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 23.0 °C |
2.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Specialty Suspension CG E 44 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Eastman CB11E PET (discontinued **)
- Inno-Comp INNOPOL® CS 4-8000 Polypropylene Random Copolymer
- Isoflon Tisoflon® 5G Polytetrafluoroethylene & Graphite Coated Glass Fabric
- Techmer ES HiFill® HDPE GF30 CC 30% Glass Filled
- A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate
- Eurostar Starflam RF0069 PA66, 30% Glass Fiber, Flame Retardant, Injection Molded
- BASF Lupranate® 5130 Isocyanate
- Hexion Bakelite™ PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties, Low Shrinkage (disconti
Copyright © lookpolymers.com All Rights Reserved