Oxford Polymers 10GF 10% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 10% Glass Fiber |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 10GF 10% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass Fiber Filled Polyetherimide for Extrusion and Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Water Absorption | 0.22 % | 0.22 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 114 MPa | 16600 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 23.0 °C |
1.10 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 382 °C | 720 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LGK5030 PC (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing
- Michelman® Michem® Lube 160 Anionic carnauba wax emulsion
- LATI Laticonther 88/10 GR/50 PEEK, 50% Graphite Reinforced
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF2919 Fluoropolymer Tape
- EMS-Grivory Grivory® BR 40 PA6
- Abatron AboCast/AboCure 50-24/8501-4 High Temperature Resistant Epoxy
- Polykemi AB POLYfill PPH TS3020 Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved