Owens Corning Glass Fiber Reinforced Epoxy (Filament Wound), 80 wt.% glass

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset
Manufacturer Owens Corning
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Owens Corning Glass Fiber Reinforced Epoxy (Filament Wound), 80 wt.% glass.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Epoxies are highly resistant to water, alkalis and organic solvents. Although standard epoxies have only a fair resistance to acids and oxidizing agents, they can be formulated for better resistance to these agents. They should be tested before use. Data provided by the manufacturer, Owens Corning.
Physical Properties Metric English Comments
Density 2.08 g/cc
0.0751 lb/in³
ASTM D792
Water Absorption 0.50 %
0.50 %
24 hrs.; ASTM D570
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 98
98
ASTM D785
Tensile Strength, Ultimate 550 MPa
79800 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Modulus of Elasticity 30.0 GPa
4350 ksi
ASTM D638
Flexural Strength 700 MPa
102000 psi
ASTM D790
Flexural Modulus 30.0 GPa
4350 ksi
ASTM D790
Compressive Strength 310 MPa
45000 psi
ASTM D695
Izod Impact, Notched 24.0 J/cm
45.0 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear 3.60 µm/m-°C

@Temperature 20.0 °C
2.00 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 0.962 J/g-°C
0.230 BTU/lb-°F
Thermal Conductivity 0.277 W/m-K
1.92 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) >= 204 °C
>= 400 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Strength 11.8 kV/mm
300 kV/in
ASTM D149