PolyOne FireCon™ CPE 30-11 RoHS BLACK Polyethylene, Chlorinated (CPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	FireCon™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne FireCon™ CPE 30-11 RoHS BLACK Polyethylene, Chlorinated (CPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CPE-30-11 RoHS BLACK is a heavy duty thermoplastic jacket for power and control cables. It is suitable for VW1 and tray fire rated applications. CPE-30-11 RoHS BLACK offers high tensile and superior fluid resistance.Note: Pre-drying is recommended for 4 hours at 175°-185°F. Note: Typical processing temperatures range between 320°-390°F depending upon screw design. Contact Technical Service for recommendation for specific equipment. NOTE: Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.29 g/cc	1.29 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	41	41	10 sec; ASTM D2240
Tensile Strength at Break	11.7 MPa	1700 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	350 %	350 %	Type IV, 510 mm/min; ASTM D638
Tensile Modulus	0.00827 GPa	1.20 ksi	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-35.0 °C	-31.0 °F	ASTM D746
Oxygen Index	30 % @Thickness 1.91 mm	30 % @Thickness 0.0752 in	ASTM D2863

Descriptive Properties	Value	Comments
Appearance	Pellets/Cubes	ASTM D2090
Features	Flame Retardant
Forms	Pellets
Generic Material	CPE
Generic Name	Polyethylene, Chlorinated (CPE)
Regional Availability	Asia Pacific
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Cable Jacketing
	Wire & Cable Applications