Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled

Category	Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.39 - 1.81 g/cc	0.0502 - 0.0654 lb/in³	Average value: 1.70 g/cc Grade Count:43
Filler Content	40.0 %	40.0 %	Average value: 40.0 % Grade Count:8
Water Absorption	0.0200 - 0.100 %	0.0200 - 0.100 %	Average value: 0.0450 % Grade Count:4
Moisture Absorption at Equilibrium	0.00200 - 0.0400 %	0.00200 - 0.0400 %	Average value: 0.0108 % Grade Count:10
Water Absorption at Saturation	0.00400 - 0.0700 %	0.00400 - 0.0700 %	Average value: 0.0247 % Grade Count:9
Linear Mold Shrinkage	0.000 - 0.00400 cm/cm	0.000 - 0.00400 in/in	Average value: 0.00126 cm/cm Grade Count:39
Linear Mold Shrinkage, Transverse	0.00200 - 0.0120 cm/cm	0.00200 - 0.0120 in/in	Average value: 0.00545 cm/cm Grade Count:34

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	44.0 - 96.0	44.0 - 96.0	Average value: 64.8 Grade Count:8
Tensile Strength, Ultimate	3.00 - 177 MPa	435 - 25700 psi	Average value: 114 MPa Grade Count:45
	9.28 - 138 MPa @Temperature -20.0 - 200 °C	1350 - 20000 psi @Temperature -4.00 - 392 °F	Average value: 49.7 MPa Grade Count:1
	9.28 - 138 MPa @Strain 0.230 - 4.21 %	1350 - 20000 psi @Strain 0.230 - 4.21 %	Average value: 49.7 MPa Grade Count:1
Elongation at Break	0.500 - 3.60 %	0.500 - 3.60 %	Average value: 1.95 % Grade Count:44
Modulus of Elasticity	7.50 - 34.5 GPa	1090 - 5000 ksi	Average value: 14.7 GPa Grade Count:45
Flexural Yield Strength	109 - 250 MPa	15800 - 36300 psi	Average value: 180 MPa Grade Count:45
Flexural Modulus	7.20 - 27.6 GPa	1040 - 4000 ksi	Average value: 14.0 GPa Grade Count:45
Compressive Yield Strength	53.0 - 134 MPa	7690 - 19400 psi	Average value: 101 MPa Grade Count:7
Compressive Modulus	7.70 - 18.0 GPa	1120 - 2610 ksi	Average value: 13.2 GPa Grade Count:7
Izod Impact, Notched	0.534 - 1.12 J/cm	1.00 - 2.10 ft-lb/in	Average value: 0.798 J/cm Grade Count:6
Izod Impact, Unnotched	2.67 - 4.27 J/cm	5.00 - 8.00 ft-lb/in	Average value: 3.38 J/cm Grade Count:3
Izod Impact, Notched (ISO)	3.50 - 60.0 kJ/m²	1.67 - 28.6 ft-lb/in²	Average value: 17.0 kJ/m² Grade Count:27
Izod Impact, Unnotched (ISO)	20.0 - 45.0 kJ/m²	9.52 - 21.4 ft-lb/in²	Average value: 26.3 kJ/m² Grade Count:6
	20.0 - 20.0 kJ/m² @Temperature -30.0 - -30.0 °C	9.52 - 9.52 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 20.0 kJ/m² Grade Count:2
Charpy Impact Unnotched	1.30 - 5.50 J/cm²	6.19 - 26.2 ft-lb/in²	Average value: 3.10 J/cm² Grade Count:19
	1.80 - 4.00 J/cm² @Temperature -30.0 - 30.0 °C	8.57 - 19.0 ft-lb/in² @Temperature -22.0 - 86.0 °F	Average value: 2.45 J/cm² Grade Count:4
Charpy Impact, Notched	0.400 - 3.00 J/cm²	1.90 - 14.3 ft-lb/in²	Average value: 1.21 J/cm² Grade Count:30
	0.600 - 1.50 J/cm² @Temperature -30.0 - 30.0 °C	2.86 - 7.14 ft-lb/in² @Temperature -22.0 - 86.0 °F	Average value: 1.27 J/cm² Grade Count:4

Thermal Properties	Metric	English	Comments
CTE, linear	1.00 - 23.0 µm/m-°C	0.556 - 12.8 µin/in-°F	Average value: 5.74 µm/m-°C Grade Count:31
	-2.00 - 3.00 µm/m-°C @Temperature 55.0 - 320 °C	-1.11 - 1.67 µin/in-°F @Temperature 131 - 608 °F	Average value: 1.79 µm/m-°C Grade Count:2
	-2.00 - 5.00 µm/m-°C @Temperature 55.0 - 320 °C	-1.11 - 2.78 µin/in-°F @Temperature 131 - 608 °F	Average value: 1.79 µm/m-°C Grade Count:4
	-2.00 - 5.00 µm/m-°C @Thickness 2.00 - 4.00 mm	-1.11 - 2.78 µin/in-°F @Thickness 0.0787 - 0.157 in	Average value: 1.79 µm/m-°C Grade Count:4
CTE, linear, Transverse to Flow	11.0 - 82.0 µm/m-°C	6.11 - 45.6 µin/in-°F	Average value: 52.4 µm/m-°C Grade Count:31
	71.0 - 88.0 µm/m-°C @Temperature 55.0 - 320 °C	39.4 - 48.9 µin/in-°F @Temperature 131 - 608 °F	Average value: 84.1 µm/m-°C Grade Count:2
	71.0 - 94.0 µm/m-°C @Temperature 55.0 - 320 °C	39.4 - 52.2 µin/in-°F @Temperature 131 - 608 °F	Average value: 84.1 µm/m-°C Grade Count:4
	71.0 - 94.0 µm/m-°C @Thickness 2.00 - 4.00 mm	39.4 - 52.2 µin/in-°F @Thickness 0.0787 - 0.157 in	Average value: 84.1 µm/m-°C Grade Count:4
Melting Point	280 - 357 °C	536 - 675 °F	Average value: 331 °C Grade Count:35
Deflection Temperature at 0.46 MPa (66 psi)	250 - 286 °C	482 - 547 °F	Average value: 271 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi)	215 - 356 °C	419 - 673 °F	Average value: 267 °C Grade Count:45
Deflection Temperature at 8.0 MPa	119 - 267 °C	246 - 513 °F	Average value: 191 °C Grade Count:8
Vicat Softening Point	146 - 239 °C	295 - 462 °F	Average value: 196 °C Grade Count:9
UL RTI, Electrical	130 - 240 °C	266 - 464 °F	Average value: 191 °C Grade Count:5
UL RTI, Mechanical with Impact	130 - 220 °C	266 - 428 °F	Average value: 180 °C Grade Count:5
UL RTI, Mechanical without Impact	130 - 240 °C	266 - 464 °F	Average value: 199 °C Grade Count:4
Flammability, UL94	V-0	V-0	Grade Count:29

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1e+05 - 1.00e+17 ohm-cm	1e+05 - 1.00e+17 ohm-cm	Average value: 9.72e+15 ohm-cm Grade Count:24
Surface Resistance	1.00e+7 - 1.00e+17 ohm	1.00e+7 - 1.00e+17 ohm	Average value: 2.12e+16 ohm Grade Count:26
Dielectric Constant	3.10 - 4.97	3.10 - 4.97	Average value: 3.89 Grade Count:21
Dielectric Strength	22.6 - 59.0 kV/mm	575 - 1500 kV/in	Average value: 36.2 kV/mm Grade Count:17
Dissipation Factor	0.00200 - 70.0	0.00200 - 70.0	Average value: 7.02 Grade Count:22
Arc Resistance	130 - 180 sec	130 - 180 sec	Average value: 156 sec Grade Count:5
Comparative Tracking Index	150 - 249 V	150 - 249 V	Average value: 182 V Grade Count:20

Processing Properties	Metric	English	Comments
Processing Temperature	20.0 - 391 °C	68.0 - 735 °F	Average value: 172 °C Grade Count:31