Overview of materials for Ethylene-Methyl Acrylate Copolymer, Molding Grade
| Category | Polymer , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Overview of materials for Ethylene-Methyl Acrylate Copolymer, Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Molding Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 - 0.945 g/cc | 0.0335 - 0.0341 lb/in³ | Average value: 0.939 g/cc Grade Count:17 |
| Methyl Acrylate Content | 16.5 - 24.0 % | 16.5 - 24.0 % | Average value: 21.5 % Grade Count:7 |
| Melt Flow | 0.400 - 135 g/10 min | 0.400 - 135 g/10 min | Average value: 12.7 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75.0 - 98.0 | 75.0 - 98.0 | Average value: 84.8 Grade Count:15 |
| Hardness, Shore D | 19.0 - 47.0 | 19.0 - 47.0 | Average value: 32.8 Grade Count:15 |
| Tensile Strength, Ultimate | 2.83 - 14.0 MPa | 410 - 2030 psi | Average value: 10.7 MPa Grade Count:15 |
| Elongation at Break | 575 - 860 % | 575 - 860 % | Average value: 751 % Grade Count:15 |
| Modulus of Elasticity | 0.0180 - 0.0800 GPa | 2.61 - 11.6 ksi | Average value: 0.0474 GPa Grade Count:9 |
| Flexural Modulus | 0.0217 - 0.0572 GPa | 3.15 - 8.30 ksi | Average value: 0.0336 GPa Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 72.2 - 102 °C | 162 - 216 °F | Average value: 87.9 °C Grade Count:17 |
| Vicat Softening Point | 37.2 - 78.0 °C | 99.0 - 172 °F | Average value: 53.1 °C Grade Count:17 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Adapter Temperature | 180 - 290 °C | 356 - 554 °F | Average value: 240 °C Grade Count:9 |
| Die Temperature | 180 - 290 °C | 356 - 554 °F | Average value: 240 °C Grade Count:9 |
| Melt Temperature | 150 - 290 °C | 302 - 554 °F | Average value: 194 °C Grade Count:9 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF1020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Lucent Polymers GPB-115 Polybutylene Terephthalate, 15% Glass Fiber Reinforced
- Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF)
- Saint-Gobain Chemfab® 3790 Open Mesh Belting
- Techmer ES Electrafil® J-1200/CF/30 ABS, 30% Carbon Fiber Reinforced
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- Aremco AREMCOLOX™ 502-1400 (Full-Fired) Dense Alumina
- Aremco Corr-Paint™ CP2020 High Temperature Protective Coating Urethane, Aluminum Filled
- Overview of materials for Acetal Homopolymer, PTFE-Filled
- LATI Latilub 66-20T G/40 PA66, 40% Glass Fiber Reinforced, PTFE Filled
Copyright © lookpolymers.com All Rights Reserved