Overview of materials for Acrylonitrile Butadiene Styrene (ABS), NCG Fiber Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), NCG Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), NCG Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), NCG Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.07 - 1.51 g/cc
0.0387 - 0.0546 lb/in³
Average value: 1.30 g/cc Grade Count:18
Filler Content 5.00 - 40.0 %
5.00 - 40.0 %
Average value: 18.9 % Grade Count:18
Water Absorption 0.120 - 0.500 %
0.120 - 0.500 %
Average value: 0.223 % Grade Count:11
Linear Mold Shrinkage 0.000100 - 0.00300 cm/cm
0.000100 - 0.00300 in/in
Average value: 0.00150 cm/cm Grade Count:18
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107 - 110
107 - 110
Average value: 109 Grade Count:4
Tensile Strength, Ultimate 44.8 - 121 MPa
6500 - 17500 psi
Average value: 69.7 MPa Grade Count:18
Elongation at Break 1.00 - 2.00 %
1.00 - 2.00 %
Average value: 1.41 % Grade Count:18
Modulus of Elasticity 5.17 - 17.9 GPa
750 - 2600 ksi
Average value: 8.75 GPa Grade Count:18
Flexural Yield Strength 72.4 - 138 MPa
10500 - 20000 psi
Average value: 103 MPa Grade Count:18
Flexural Modulus 4.48 - 17.2 GPa
650 - 2500 ksi
Average value: 7.75 GPa Grade Count:18
Compressive Yield Strength 48.3 - 58.6 MPa
7000 - 8500 psi
Average value: 53.4 MPa Grade Count:4
Izod Impact, Notched 0.374 - 0.801 J/cm
0.700 - 1.50 ft-lb/in
Average value: 0.605 J/cm Grade Count:18
Izod Impact, Unnotched 1.60 - 2.67 J/cm
3.00 - 5.00 ft-lb/in
Average value: 2.21 J/cm Grade Count:18
Thermal Properties Metric English Comments
CTE, linear 32.4 - 50.4 µm/m-°C
18.0 - 28.0 µin/in-°F
Average value: 39.0 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 110 - 118 °C
230 - 245 °F
Average value: 111 °C Grade Count:13
Deflection Temperature at 1.8 MPa (264 psi) 104 - 116 °C
220 - 240 °F
Average value: 106 °C Grade Count:13
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:15
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 - 100 ohm-cm
1.00 - 100 ohm-cm
Average value: 21.1 ohm-cm Grade Count:17
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
Average value: 72900 ohm Grade Count:14
Static Decay 2.00 sec
2.00 sec
Average value: 2.00 sec Grade Count:13
Processing Properties Metric English Comments
Processing Temperature 199 - 238 °C
390 - 460 °F
Average value: 220 °C Grade Count:13
Melt Temperature 204 - 238 °C
400 - 460 °F
Average value: 221 °C Grade Count:5
Mold Temperature 62.8 - 85.0 °C
145 - 185 °F
Average value: 73.9 °C Grade Count:18
Drying Temperature 82.2 °C
180 °F
Average value: 82.2 °C Grade Count:5
Moisture Content 0.100 %
0.100 %
Average value: 0.100 % Grade Count:5
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:5
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:18