Outokumpu 725LN Austenitic Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel |
| Manufacturer | Outokumpu |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Outokumpu 725LN Austenitic Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.00 g/cc | 0.289 lb/in³ | RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 630 MPa | 91400 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
| 290 MPa @Strain 0.200 % |
42100 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| 320 MPa @Strain 1.00 % |
46400 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| 135 MPa @Strain 0.200 %, Temperature 400 °C |
19600 psi @Strain 0.200 %, Temperature 752 °F |
EN min.; EN 10002-5 | |
| 160 MPa @Strain 0.200 %, Temperature 200 °C |
23200 psi @Strain 0.200 %, Temperature 392 °F |
EN min.; EN 10002-5 | |
| 195 MPa @Strain 0.200 %, Temperature 100 °C |
28300 psi @Strain 0.200 %, Temperature 212 °F |
EN min.; EN 10002-5 | |
| Elongation at Break | 55 % | 55 % | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Modulus of Elasticity | 200 GPa | 29000 ksi | RT |
| 170 GPa @Temperature 400 °C |
24700 ksi @Temperature 752 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.5 µm/m-°C @Temperature 100 °C |
8.61 µin/in-°F @Temperature 212 °F |
|
| 17.0 µm/m-°C @Temperature 400 °C |
9.44 µin/in-°F @Temperature 752 °F |
||
| Specific Heat Capacity | 0.440 J/g-°C | 0.105 BTU/lb-°F | RT |
| Thermal Conductivity | 12.0 W/m-K | 83.3 BTU-in/hr-ft²-°F | RT |
| 17.0 W/m-K @Temperature 400 °C |
118 BTU-in/hr-ft²-°F @Temperature 752 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.020 % | 0.020 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 50.65 % | 50.65 % | |
| Molybdenum, Mo | 2.2 % | 2.2 % | |
| Nickel, Ni | 22 % | 22 % | |
| Nitrogen, N | 0.13 % | 0.13 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000750 ohm-cm | 0.0000750 ohm-cm | RT |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer (Asia Pacific)
- DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7373 PEEK, with carbon fiber, lubricant modified
- Styron DL 239NA Carboxylated SB
- A. Schulman POLYBATCH™ Orange 1096 Concentrate Based In Polyethylene
- DuPont Performance Polymers Zytel® HTN 51G45HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
- Colorite Polymers 8533 General Purpose Vinyl Compound
- Brandenburger BL 70 Slide Bearing Material
Copyright © lookpolymers.com All Rights Reserved