Outokumpu 4571 Cr-Ni-Mo Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4571 Cr-Ni-Mo Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Very good corrosion resistance, weldable, and resistant to sensitization.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell 165
165
Outokumpu Typical, 20°C, Hot rolled plate (Quarto)/Cold rolled strip/sheet; EN 10003-1
Tensile Strength, Ultimate 570 MPa
82700 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
360 MPa

@Temperature 500 °C
 52200 psi

@Temperature 932 °F
 EN min.; EN 10002-5
375 MPa

@Temperature 300 °C
 54400 psi

@Temperature 572 °F
 EN min.; EN 10002-5
375 MPa

@Temperature 400 °C
 54400 psi

@Temperature 752 °F
 EN min.; EN 10002-5
390 MPa

@Temperature 200 °C
 56600 psi

@Temperature 392 °F
 EN min.; EN 10002-5
440 MPa

@Temperature 100 °C
 63800 psi

@Temperature 212 °F
 EN min.; EN 10002-5
840 MPa

@Temperature -80.0 °C
 122000 psi

@Temperature -112 °F
 EN min; EN 10002-5
1200 MPa

@Temperature -196 °C
 174000 psi

@Temperature -321 °F
 EN min; EN 10002-5
Tensile Strength, Yield 220 MPa

@Strain 0.200 %
 31900 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
270 MPa

@Strain 0.200 %
 39200 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
310 MPa

@Strain 1.00 %
 45000 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
129 MPa

@Strain 0.200 %,
Temperature 500 °C
 18700 psi

@Strain 0.200 %,
Temperature 932 °F
 EN min.; EN 10002-5
135 MPa

@Strain 0.200 %,
Temperature 400 °C
 19600 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
145 MPa

@Strain 0.200 %,
Temperature 300 °C
 21000 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
158 MPa

@Strain 1.00 %,
Temperature 500 °C
 22900 psi

@Strain 1.00 %,
Temperature 932 °F
 EN min.; EN 10002-5
164 MPa

@Strain 1.00 %,
Temperature 400 °C
 23800 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
167 MPa

@Strain 0.200 %,
Temperature 200 °C
 24200 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
175 MPa

@Strain 1.00 %,
Temperature 300 °C
 25400 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
185 MPa

@Strain 0.200 %,
Temperature 100 °C
 26800 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
196 MPa

@Strain 1.00 %,
Temperature 200 °C
 28400 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
218 MPa

@Strain 1.00 %,
Temperature 100 °C
 31600 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
275 MPa

@Strain 0.200 %,
Temperature -80.0 °C
 39900 psi

@Strain 0.200 %,
Temperature -112 °F
 EN min.; EN 10002-5
350 MPa

@Strain 0.200 %,
Temperature -196 °C
 50800 psi

@Strain 0.200 %,
Temperature -321 °F
 EN min.; EN 10002-5
355 MPa

@Strain 1.00 %,
Temperature -80.0 °C
 51500 psi

@Strain 1.00 %,
Temperature -112 °F
 EN min.; EN 10002-5
450 MPa

@Strain 1.00 %,
Temperature -196 °C
 65300 psi

@Strain 1.00 %,
Temperature -321 °F
 EN min.; EN 10002-5
Elongation at Break 50 %
50 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
35 %

@Temperature -196 °C
 35 %

@Temperature -321 °F
 EN min
40 %

@Temperature -80.0 °C
 40 %

@Temperature -112 °F
 EN min
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa

@Temperature 500 °C
 23900 ksi

@Temperature 932 °F
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
179 GPa

@Temperature 300 °C
 26000 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.5 µm/m-°C

@Temperature 100 °C
 9.17 µin/in-°F

@Temperature 212 °F
17.5 µm/m-°C

@Temperature 200 °C
 9.72 µin/in-°F

@Temperature 392 °F
18.0 µm/m-°C

@Temperature 300 °C
 10.0 µin/in-°F

@Temperature 572 °F
18.5 µm/m-°C

@Temperature 400 °C
 10.3 µin/in-°F

@Temperature 752 °F
19.0 µm/m-°C

@Temperature 500 °C
 10.6 µin/in-°F

@Temperature 932 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.040 %
0.040 %
Chromium, Cr 16.8 %
16.8 %
Iron, Fe 70.16 %
70.16 %
Molybdenum, Mo 2.1 %
2.1 %
Nickel, Ni 10.9 %
10.9 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000750 ohm-cm
0.0000750 ohm-cm
RT