Outokumpu 2205 Duplex Stainless Steel

Category Metal , Ferrous Metal , Duplex , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 2205 Duplex Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Duplex stainless combining high mechanical strength with good corrosion resistance.Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesComponents for structural designStorage tanksPressure vesselsHeat exchangersWater heatersRotors, impellers and shaftsAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 7.80 g/cc
0.282 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 750 MPa
109000 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
540 MPa

@Temperature 250 °C
 78300 psi

@Temperature 482 °F
 EN min.; EN 10002-5
550 MPa

@Temperature 200 °C
 79800 psi

@Temperature 392 °F
 EN min.; EN 10002-5
570 MPa

@Temperature 150 °C
 82700 psi

@Temperature 302 °F
 EN min.; EN 10002-5
590 MPa

@Temperature 100 °C
 85600 psi

@Temperature 212 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 460 MPa

@Strain 0.200 %
 66700 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
510 MPa

@Strain 0.200 %
 74000 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
300 MPa

@Strain 0.200 %,
Temperature 250 °C
 43500 psi

@Strain 0.200 %,
Temperature 482 °F
 EN min.; EN 10002-5
315 MPa

@Strain 0.200 %,
Temperature 200 °C
 45700 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
335 MPa

@Strain 0.200 %,
Temperature 150 °C
 48600 psi

@Strain 0.200 %,
Temperature 302 °F
 EN min.; EN 10002-5
360 MPa

@Strain 0.200 %,
Temperature 100 °C
 52200 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
Elongation at Break 35 %
35 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Modulus of Elasticity 200 GPa
29000 ksi
RT
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
180 GPa

@Temperature 300 °C
 26100 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Fatigue Strength 767 MPa
111000 psi
R=smin/smax=0.1; 2 million cycles, F50
510 MPa

@# of Cycles 2.00e+6
74000 psi

@# of Cycles 2.00e+6
R=smin/smax=0.1;RT; 50% probability of failure
497 MPa

@Strain 0.200 %
 72100 psi

@Strain 0.200 %
 R=smin/smax=0.1; 2 million cycles, F50
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
EN 10045-1
>= 40.0 J

@Temperature -40.0 °C
 >= 29.5 ft-lb

@Temperature -40.0 °F
 EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Temperature 100 °C
 7.22 µin/in-°F

@Temperature 212 °F
14.5 µm/m-°C

@Temperature 400 °C
 8.06 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
0.530 J/g-°C

@Temperature 100 °C
 0.127 BTU/lb-°F

@Temperature 212 °F
0.560 J/g-°C

@Temperature 200 °C
 0.134 BTU/lb-°F

@Temperature 392 °F
0.590 J/g-°C

@Temperature 300 °C
 0.141 BTU/lb-°F

@Temperature 572 °F
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
16.0 W/m-K

@Temperature 100 °C
 111 BTU-in/hr-ft²-°F

@Temperature 212 °F
17.0 W/m-K

@Temperature 200 °C
 118 BTU-in/hr-ft²-°F

@Temperature 392 °F
18.0 W/m-K

@Temperature 300 °C
 125 BTU-in/hr-ft²-°F

@Temperature 572 °F
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 22 %
22 %
Iron, Fe 69.01 %
69.01 %
Molybdenum, Mo 3.1 %
3.1 %
Nickel, Ni 5.7 %
5.7 %
Nitrogen, N 0.17 %
0.17 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000800 ohm-cm
0.0000800 ohm-cm
RT
0.0000850 ohm-cm

@Temperature 100 °C
 0.0000850 ohm-cm

@Temperature 212 °F
0.0000900 ohm-cm

@Temperature 200 °C
 0.0000900 ohm-cm

@Temperature 392 °F
0.000100 ohm-cm

@Temperature 300 °C
 0.000100 ohm-cm

@Temperature 572 °F
Processing Properties Metric English Comments
Annealing Temperature 1020 - 1100 °C
1870 - 2010 °F
Quench Annealing
1020 - 1100 °C
1870 - 2010 °F
Stress Relief Annealing