Noltex Soarnol® ST110 Ethylene Vinyl Alcohol Copolymer

Category Polymer , Thermoplastic , Ethylene Vinyl Alcohol (EVOH)
Manufacturer Noltex
Trade Name Soarnol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Noltex Soarnol® ST110 Ethylene Vinyl Alcohol Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified DC3203; improved flex crack resistance and thermoformability. Ethylene content 32 mol%. Volatile matter 0.3%.The gas barrier property of Soarnol is about forty times better than that of nylon, therefore, Soarnol allows design of lower cost packages by using a thin gas barrier layer without loss of shelf life.Soarnol ST110 has an excellent flex crack resistance and stretchability without lower of gas barrier property. This grade is appropriate for bag-in-box and stretched film. Information provided by Soarus, LLC. In the United States SOARNOL is produced by Noltex, L.L.C., an affiliate of Nippon Gohsei.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Moisture Vapor Transmission 1.74 cc-mm/m²-24hr-atm
4.42 cc-mil/100 in²-24hr-atm
40°C- 90% RH; based on 30 µm layer
Oxygen Transmission 0.0240 cc-mm/m²-24hr-atm
0.0610 cc-mil/100 in²-24hr-atm
20°C- 65% RH; based on 20 µm layer
Viscosity 170000 cP

@Shear Rate 60.0 1/s,
Temperature 200 °C
170000 cP

@Shear Rate 60.0 1/s,
Temperature 392 °F
Melt Flow 3.7 g/10 min

@Load 2.16 kg,
Temperature 210 °C
3.7 g/10 min

@Load 4.76 lb,
Temperature 410 °F
Thermal Properties Metric English Comments
Melting Point 183 °C
361 °F
DSC, both heating and cooling speeds of 20°C/min
Crystallization Temperature 160 °C
320 °F
DSC, both heating and cooling speeds of 20°C/min
Glass Transition Temp, Tg 61.0 °C
142 °F
DSC, both heating and cooling speeds of 20°C/min
Optical Properties Metric English Comments
Refractive Index 1.524
1.524
Quenched
1.533
1.533
Annealed at 140°C, 30 min