- Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled
Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.03 g/cc | 0.0733 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 - 1.0 % | 0.50 - 1.0 % | ISO 62 |
| Water Absorption at Saturation | 1.0 - 2.0 % | 1.0 - 2.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0030 - 0.010 cm/cm | 0.0030 - 0.010 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 155 MPa | 22500 psi | ISO 2039-1 |
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 6.80 GPa | 986 ksi | ISO 527 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 7.05 GPa | 1020 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | DIN 53453 |
| 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU | |
| 2.20 J/cm² @Temperature -40.0 °C |
10.5 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² | 3.81 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 160 °C | 320 °F | Continuous; FRISETTA Test Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | IEC 93 |
Users viewing this material also viewed the following:
- LyondellBasell Lupolen® 2425 K LDPE, Film Grade
- LG Chemical EM600A Impact modifier for Engineering Plastics
- SABIC Innovative Plastics LNP LUBRICOMP KA000M POM (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SGH 5500 Polyvinyl Chloride, Flexible
- Eagle Brass 110 EPT COPPER, Extra Hard
- Elektro-Isola Etronit IS Phenolic, Paper Reinforcement, Dark Brown, Sheets
- Entec Hypro™ PPH-GF10 Natural Homopolymer Polypropylene, 10% Glass Reinforced
- Chosun Refractories SB65S Bricks, Oxide Bonded SiC
- Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded
- Beijing Evergrow Resources UHF-BF1300 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved