Nilit FRIANYL A63 BR80 Nylon 6.6 for injection molding, 80% bronze filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 BR80 Nylon 6.6 for injection molding, 80% bronze filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.80 g/cc | 0.137 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 - 0.80 % | 0.30 - 0.80 % | ISO 62 |
| Water Absorption at Saturation | 1.0 - 2.0 % | 1.0 - 2.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0020 - 0.0070 cm/cm | 0.0020 - 0.0070 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 32 % | 32 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | DIN 53453 |
| 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179/1eU | |
| 1.90 J/cm² @Temperature -40.0 °C |
9.04 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| 0.300 J/cm² | 1.43 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Continuous; FRISETTA Test Method |
Users viewing this material also viewed the following:
- Okulen® 1000 PE-UHMW, Colored
- SABIC Innovative Plastics EXTEM XH1015 TPI Resin
- SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific)
- Stir SpA RH X (PVC)
- SMAC SMACMOUNT® 1195S Damping Material
- Covestro Makrolon® XT5010 Polycarbonate
- Chi Mei Polyrex® PH-55Y Polystyrene - Food
- Bohler-Uddeholm BÖHLER K340 ISODUR® Premium Cold Work Steel
- Arlon 31570R025 0.025" (0.635 mm) Uncured Unsupported Silicone on a HDPE Carrier
- Trelleborg Emerson & Cuming Stycast® XT-1169 Two-Component Epoxy High Service Temp Encapsulant
Copyright © lookpolymers.com All Rights Reserved