Nanocyl PLASTICYL™ PC1501 Polycarbonate with 2 wt% Multi-Wall Carbon Nanotubes

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Conductive
Manufacturer	Nanocyl
Trade Name	PLASTICYL™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nanocyl PLASTICYL™ PC1501 Polycarbonate with 2 wt% Multi-Wall Carbon Nanotubes.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PLASTICYL™ is a family of Multi-Wall Carbon Nanotube (MWNT) thermoplastic concentrates for applications requiring superior electrical conductivity and electrostatic discharge (ESD) properties. PLASTICYL™ PC1501 is a conductive masterbatch based on polycarbonate. Because of its low viscosity and high flow formulation, PLASTICYL™ PC1501 is ideal for standard injection molding and extrusion processes.Key Applications:E&E, automotive and packaging industriesHDD (hard disk drive) internal componentsHDD and IC handling traysBenefits:Excellent electrical conductivity at low loadingExcellent surface cleanlinessRetention of key mechanical propertiesEase of processing

Physical Properties	Metric	English	Comments
Filler Content	2 %	2 %	Carbon Nanotube Loading
Melt Flow	16.9 g/10 min @Load 1.20 kg, Temperature 300 °C	16.9 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133:1997

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527-1,2
Tensile Modulus	2.584 GPa	374.8 ksi	ISO 527-1,2
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	ISO 180

Electrical Properties	Metric	English	Comments
Volume Resistivity	54 ohm-cm	54 ohm-cm	3.0 wt% carbon nanotubes in PC; CTM E043
	100 ohm-cm	100 ohm-cm	2.5 wt% carbon nanotubes in PC; CTM E043
	1200 ohm-cm	1200 ohm-cm	2.0 wt% carbon nanotubes in PC; CTM E043
	30000 ohm-cm	30000 ohm-cm	1.5 wt% carbon nanotubes in PC; CTM E043
Surface Resistivity per Square	1200 ohm	1200 ohm	3.0 wt% carbon nanotubes in PC; CTM E042
	4000 ohm	4000 ohm	2.5 wt% carbon nanotubes in PC; CTM E042
	17000 ohm	17000 ohm	2.0 wt% carbon nanotubes in PC; CTM E042
	800000 ohm	800000 ohm	1.5 wt% carbon nanotubes in PC; CTM E042

Processing Properties	Metric	English	Comments
Processing Temperature	300 °C	572 °F	Material Temperature
Mold Temperature	120 °C	248 °F
Hold Pressure	45.0 MPa	6530 psi
Back Pressure	4.00 MPa	580 psi

Descriptive Properties	Value	Comments
Processing: Holding Time	8 s
Processing: Injection Speed	30 cm³/s
Processing: Plasticizing Speed	0.4 m/s